摘要
It is of great significance to obtain a thorough understanding of the physical mechanisms responsible for humping bead phenomenon in high speed gas metal arc welding （GMAW） in order to raise welding efficiency. Experiments were conducted to observe the weld pool behaviors in high speed GMAW, and it was found that both the severely deformed weld pool surface and strong backward flowing play a dominant role in humping bead formation. In this study, a mathematical model is developed to quantitatively analyze the forming mechanism of humping beads for high speed GMAW through considering both the momentum and heat content distribution of the backward flowing molten metal inside the weld pool. The transient development of temperature profiles in the weld pool with severe deformation demonstrates the humping bead forming process under some welding conditions. The predicted and measured humping bead dimensions are in agreement.
It is of great significance to obtain a thorough understanding of the physical mechanisms responsible for humping bead phenomenon in high speed gas metal arc welding （GMAW） in order to raise welding efficiency. Experiments were conducted to observe the weld pool behaviors in high speed GMAW, and it was found that both the severely deformed weld pool surface and strong backward flowing play a dominant role in humping bead formation. In this study, a mathematical model is developed to quantitatively analyze the forming mechanism of humping beads for high speed GMAW through considering both the momentum and heat content distribution of the backward flowing molten metal inside the weld pool. The transient development of temperature profiles in the weld pool with severe deformation demonstrates the humping bead forming process under some welding conditions. The predicted and measured humping bead dimensions are in agreement.
作者简介
E-mail： wucs@sdu.edu.cn