摘要
采用微波水热法,以CdCl2.H2O和Na2S2O3.5H2O为镉源和硫源,分别以柠檬酸、乙二胺四乙酸(EDTA)、六亚甲基四胺(乌洛托品)和聚乙烯吡咯烷酮(PVP)为模板剂,合成了不同微观形貌的硫化镉微晶。利用X射线衍射仪(XRD)、扫描电子显微镜(SEM)、EDS、透射电子显微镜(TEM)等对样品的物相、形貌和元素组成进行了分析。结果表明:通过添加不同模板剂制备了球形、花状和棒状硫化镉微晶,制备的硫化镉微晶结晶良好;紫外-可见吸收光谱分析表明,产物均发生了不同程度的蓝移。
Cadmium sulphide（CdS） microcrystallites with different morphology had been prepared by microwave hydrothermal（M-H） process using cadmium chloride and sodium thiosulfate as raw materials and citric acid,ethylene diamine tetraacetic acid（EDTA）,hexamethylenetetramine and polyvinylpyrrolidone（PVP） as template.The products were characterized by X-ray diffraction（XRD）,scanning electron microscopy（SEM）,EDS and transmission electron microscopy（TEM）.The optical properties of the prepared CdS microcrystallites with varied shape were characterized by ultraviolet-vis.The results show that the spherical,flower-like and rod-like CdS crystals could be prepared using different templates,and the as-prepared products are well crystallized.Obvious blue-shift are observed in the UV-Vis absorption of CdS products.
出处
《人工晶体学报》
EI
CAS
CSCD
北大核心
2011年第1期139-143,共5页
Journal of Synthetic Crystals
基金
国家自然科学基金(50942047)资助项目
教育部新世纪优秀人才支持计划基金(NECT-06-0893)
教育部博士点基金(20070708001)
陕西省自然科学基金(2010JM6001)资助项目
陕西科技大学科研创新团队基金(TD09-05)
陕西科技大学博士科研基金(BS08-09)
陕西科技大学研究生创新基金
关键词
CdS微晶
微波水热
模板剂
形貌
CdS microcrystalline
microwave hydrothermal process
template
morphology