摘要
利用低温剪切浇注半固态浆料制备技术(LSPSF),进行了A356铝合金大体积半固态浆料制备试验。从浇注量、输送管转速和冷却速度等角度,研究了A356大体积半固态组织的变化,分析了其非枝晶组织的形成和演变机理。结果表明,利用LSPSF技术,可制得品质较好的A356大体积半固态浆料,该浆料初生晶粒具有近球状的非枝晶组织特征,初生晶粒的等效直径为54.0～93.6μm,形状因子为0.74～0.84,制浆效率可达1kg/s。
Semi-solid A356 aluminum alloy slurry with large volume was prepared by LSPSF.Effects of some processing parameters,such as pouring volume,rotating speed of the duct and cooling rate,on primary phase in microstructure of the prepared slurry were examined,and formation and evolution mechanism of the non-dendrite were described.The results show that A356 semi-solid slurry with large volume and desirable quality can be prepared by the LSPSF.The primary phase in the slurry exhibits near spherical non-dendrite structure,and average equivalent diameter and shape factor of the primary phase can make 54~93.6 μm and 0.74~0.84,respectively.Meanwhile,efficiency of prepared slurry about 1 kg/s can be achieved.
出处
《特种铸造及有色合金》
CAS
CSCD
北大核心
2011年第2期133-136,202,共4页
Special Casting & Nonferrous Alloys
基金
国家自然科学基金资助项目(50965015
51001058)
教育部重点项目(205084)
作者简介
第一作者简介：王群，男，1986年出生，硕士研究生，南昌大学机电工程学院．南昌（330031），电话：13870670343，E—mail：wangq226@163．com
通讯作者：杨湘杰，男，1960年出生，教授，南昌大学机电工程学院。南昌（330031），电话：0791-3969141，E-mail：yangxj@ncu．edu．cn