通过无模板的水热方法合成了AgLa(WO4)2树枝状纳米晶,没有表面活性剂等模板的介入,使反应变得简捷、绿色和经济.利用X射线粉末衍射、扫描电子显微镜和透射电子显微镜等手段对所得材料进行了表征,并根据实验结果提出了扩散限制生长(DLA)模型.AgLa(WO4)2树枝状纳米晶可以作为稀土离子掺杂的主体材料,这种掺杂稀土离子(Yb3+,Er3+,Tm3+)的纳米晶在980 nm激光激发下展示出丰富的上转换发光颜色.根据上转换光谱详细研究了AgLa(WO4)2∶Ln3+树枝状纳米晶在980 nm激光激发下的上转换发光性质和发光机理.
AgLa（WO4）2 dendritic nanostructures with clean surfaces were synthesized through a low-cost hydrothermal method without introducing any template or surfactant.The formation mechanism was observed for the growth of dendritic nanostructures based on the experimental process.X-ray diffraction,scanning electron microscopy,transmission electron microscopy,electron diffraction,and photoluminescence spectra were used to characterize these materials.The up-conversion luminescent properties of lanthanide ions doped AgLa（WO4）2 nanostructures are of particular interest for luminescent application.
出处
《高等学校化学学报》
SCIE
EI
CAS
CSCD
北大核心
2011年第3期508-514,共7页
Chemical Journal of Chinese Universities
基金
国家自然科学基金(批准号:21071140,21001101)
国家自然科学研究创新团队基金(批准号:20921002)资助
关键词
金属钨酸盐
稀土元素
上转换发光
Metal-tungstate
Lanthanide
Up-conversion luminescence
作者简介
联系人简介：张洪杰，男，博士，研究员，博士生导师，主要从事稀土发光材料的研究．E-mail：hongiie@ciac．jl．cn