摘要
研究了油茶果壳经水蒸气活化后,浸渍磷酸再活化对活性炭中孔结构调控的影响,制备出中孔丰富的活性炭。实验结果显示:820℃下制备的水蒸气法油茶果壳活性炭以微孔为主,BET比表面积1 076 m2/g,总孔容积0.81 cm3/g,微孔率63%,中孔率33%,亚甲基蓝吸附值180 mg/g,碘吸附值1 012 mg/g;水蒸气法油茶果壳活性炭经800℃下磷酸再活化后,可明显增加BET比表面积(1 608 m2/g)和总孔容积(1.17 cm3/g),尤其对中孔率(61%)的发展更有效,同时保留一定比例的微孔(37%),显示出更高的亚甲基蓝吸附值(330 mg/g)和碘吸附值(1 326 mg/g)。
Activated carbons from Camellia oleifera shell were prepared by steam activation and phosphoric acid re-activation to modify and enrich mesoporous structure.Results showed that,activated by steam at 820 ℃,microporous activated carbons were made with BET surface area 1 076 m2,total volume 0.81 m3/g,micropore volume rate 63 %,mesopore volume rate 33 %,methylene blue value（MB）180 mg/g and iodine value 1 012 mg/g.Based on the steam-activated carbons,phosphoric acid reactivation at 820 ℃ can significantly increase BET surface area（1 608 m2/g）and total pore volume（1.17 cm3/g）,especially enhance the development of mesopore volume（61 %）and simultaneously maintain definite proportion of micropore volume（37 %）.The prepared activated carbons showed much higher adsorption value of methylene blue（330 mg/g）and iodine value（1 326 mg/g）.
出处
《林产化学与工业》
EI
CAS
CSCD
北大核心
2010年第6期24-28,共5页
Chemistry and Industry of Forest Products
基金
"十一五"国家科技支撑计划资助(2009BADB1B03)
林业公益性行业专项资助(201004051)
环境保护部南京环境科学研究所中央级公益性科研院所基本科研业务专项资助(无编号)
关键词
油茶果壳
活性炭
孔结构
调控
Camellia oleifera shell
activated carbon
pore structure
modification
作者简介
孙康（1976－），男，安徽当涂人，博士生，研究方向：炭材料研究与应用。E-mail：sunkang0226@163．com。
通讯作者：蒋剑春（1955-），男，江苏溧阳人，研究员，博士，博士生导师，主要从事林产化学加工及生物质能源开发技术。