采用自行开发的锥桶式流变成形机(Taper barrel rheomoulding machine,简称TBR),并结合TOYOBD-900V4-T型压铸机,研究了铸造压力对AZ91D镁合金流变压铸件内部微观孔洞形态以及密度的影响。结果表明,铸造压力的增大可以明显改善流变压铸件内部微观孔洞缺陷,增大铸件密度。铸造压力小于65MPa时,压力对流变压铸件微观孔洞及密度的影响较大;而大于65MPa时,铸造压力的影响较小。
We have developed a taper barrel rheomoulding machine combining with Toyo-BD-900V4-T die casting machine to understand effects of casting pressure on micro-hole morphology and density of rheo-diecasting AZ91D magnesium alloy parts.The results reveal that increasing in casting pressure can greatly eliminate the micro-hole in rheo-diecasting parts,increasing the density.The casting pressure has directly affected the micro-hole and density of the casting with pressure less than 65 MPa,however,effects of pressure can be neglected with more than 65MPa.
出处
《特种铸造及有色合金》
CAS
CSCD
北大核心
2010年第7期630-632,共3页
Special Casting & Nonferrous Alloys
基金
国家重点基础研究发展计划(973计划)资助项目(2006CB605203)
国家高技术研究发展计划(863计划)资助项目(2006AA03Z115)
"十一五"国家科技支撑计划资助项目(2006BAE04B09-4)
作者简介
杨柳青，男，1981年出生，博士研究生，北京科技大学材料科学与工程学院，通讯地址：北京有色金属研究院有色金属602事业部，北京市新街口外大街2号（100088），电话：010-62332335，13699118050，E-mail：ylqylq1999@yahoo．com.cn