摘要
采用酰氯法,用丙烯酰氯和不同相对分子质量的聚乙二醇为原料,制备出一系列具有丙烯酰端基的聚氧乙烯大单体(PEO-A)。实验证明,较佳的原料摩尔比n(PEG)∶n(CH2CHCOCl)∶n〔(CH3CH2)3N〕=2∶1∶1。然后以聚氧乙烯大单体为端基改性剂,在氮气保护下50℃四氢呋喃溶液中分别与G1.0～G4.0聚酰胺-胺树状聚合物进行Michael加成反应96h,合成出了聚氧乙烯(PEO)链封端的非离子型聚酰胺-胺树状聚合物,并用傅立叶变换红外光谱(FTIR)、核磁共振波谱(1HNMR,13CNMR)对其组成和结构进行了表征。
A series of polyoxyethylene macromonomer（PEO-A）with terminal acryloyl-groups have been synthesized from different molecular weights of polyethylene glycol and acrylchloride as raw materials via acyl-chloride method.Results show a better molar ratio n（PEG）∶n（CH2CHCOCl）∶n〔（CH3CH2）3N〕 is 2∶1∶1.Then the PEO-terminated groups non-ionic PAMAM dendrimers were prepared via the Michael addition reaction of 96 h using PEO-A as the modifier for exterior terminal groups of PAMAM G1.0 ～ G4.0 dendrimers in the N2 atmosphere,50 ℃ THF solution,respectively.The composition and structure of the modified dendrimers have been identified via FTIR,1HNMR and 13CNMR.
出处
《精细化工》
EI
CAS
CSCD
北大核心
2010年第6期525-528,588,共5页
Fine Chemicals
基金
湖南省自然科学基金资助项目(06JJ2067)
吉首大学博士科研基金资助项目(jsdxkyzz200701)~~
关键词
聚酰胺-胺树状聚合物
聚氧乙烯大单体
MICHAEL加成反应
表面改性
功能材料
poly（amidoamine）（PAMAM）dendrimers
polyoxyethylene-macromonomer（PEO-A）
Michael addition reaction
surface modification
functional materials
作者简介
彭晓春（1964-），女（土家族），湖南省永顺县人，吉首大学教授，获博士学位，主要从事高分子合成与改性研究，电话：0743-8563911，E—mail：pnfxz@126．com。