制备了一系列无机物含量大于80%的植物纤维/吸附剂/二氧化钛复合纸板,考察了复合纸板对壬基酚聚氧乙稀醚(NP-10)水溶液的光催化降解性能.结果表明,二氧化钛复合纸板对NP-10具有优良光催化降解性能,紫外光照34h后浓度为50mg·mL-1的NP-10的降解率达80%以上,光照前后NP-10水溶液的化学需氧量(COD)的变化表明,光催化降解可导致NP-10矿化.活性炭对二氧化钛光催化降解有协同作用,其在无机粉体中的质量分数为15%时,复合纸板的光催化降解性能最好.过氧化氢可大幅提高复合纸板的光催化降解性能,其最佳浓度为20mg·mL-1.二氧化钛复合纸板在NP-10水溶液中的稳定性好,重复使用10次后其质量损失小于2%,光催化降解性能不变.
Serial composite sheets containing titanium dioxide,plant fiber and adsorbent（activated carbon,zeolite,silicate,or bentonite）were prepared,and were used for photocatalytic degradation on Nonylphenol Ethoxylate-10（NP-10）in aqueous solution.The amount of the inorganic materials in the sheets was greater than 80%.The sheets exhibited excellent photocatalytic activity for degradation of NP-10.After UV irradiation for 34 h,more than 80% of NP-10（50 mg·L^-1）was degraded,and the COD was also notably decreased,indicating that NP-10 had been mineralized.Among several adsorbents,activated carbon was the best,showing a synergistic effect with TiO2 on NP-10 degradation,and its optimal loading onto the inorganic powder inside the sheet was 15%.Hydrogen peroxide could accelerate the photocatalytic degradation of NP-10,and the optimal concentration was 20 mg·L^-1.The titanium dioxide composite sheets had good stability,and the mass loss of the sheets was less than 2% after ten recycles of photocatalytic performance.
出处
《环境科学学报》
CAS
CSCD
北大核心
2010年第6期1204-1210,共7页
Acta Scientiae Circumstantiae
基金
福建省科技厅科技计划重点项目(No.2005I007)
福建省教育厅项目(No.JB08036)~~
关键词
二氧化钛
复合纸板
壬基酚聚氧乙烯醚
光催化降解
Titanium dioxide
composite sheets
Nonylphenol Ethoxylate-10
Photocatalytic degradation
作者简介
翁景峥（1972－），男，E—mail：jackyweng@vip．163．com；