摘要
利用OM,SEM,XRD及力学性能测试等手段,研究了Sb含量对Mg-4Zn-Y合金组织及性能的影响。结果表明,含Sb铸造镁合金Mg-4Zn-Y-xSb的显微组织由基体α(Mg)、二元共晶相Mg7Zn3、三元相I(Mg3Zn6Y)和YSb组成,随着Sb含量的增加,合金晶界上二元共晶相Mg7Zn3的形态逐渐由半连续网状变为分散均匀的颗粒状。合金的拉伸强度、塑性和硬度随Sb含量的增加而提高,但Sb含量过大时合金的综合力学性能下降。
The effects of Sb content on microstructure and properties of Mg-4Zn-Y alloy were investigated by OM,SEM,XRD and mechanical property test.The results indicate that the as-cast microstructure of the alloy with Sb consists of matrix α（Mg）,dual eutectic phase,ternary phase I（Mg3Zn6Y） and YSb.The morphologies of the dual eutectic phase Mg7Zn3 on the gain boundaries change from quasi-continuous-net shape to uniformly dispersed particles with the increase of Sb content.The tensile strength,elongation,hardness increase first with the increase of Sb content,but the mechanical properties reduce at the excessive Sb content.
出处
《热加工工艺》
CSCD
北大核心
2010年第4期25-27,31,共4页
Hot Working Technology
基金
航空科学基金资助项目(2008ZF52058)
中国博士后基金资助项目(20080430221)
作者简介
刘细良（1985-），男，江西九江人，硕士研究生；电话：025-52112626；E-mail：liuxiliang347122@163．com
通讯作者：刘子利（1968-），男，山东博兴人，副教授，博士；电话：025—52112626；E—maihzililiu@sohu．com