采用一种新的阳极材料:银、铜、镍的复合金属网格阳极,利用旋涂法制成了活性层为P3HT(poly(3-hexylthiophene))∶PCBM([6,6]-phenylC61-butyricacidmethylester)的柔性衬底聚合物太阳能电池。制备了5种不同结构的柔性聚合物太阳能电池器件,将采用新型阳极材料的柔性衬底聚合物太阳能电池与传统ITO(Indium tin oxide)阳极的柔性衬底聚合物太阳能电池进行对比,发现新型阳极材料所制成的器件性能得到大幅度的提高,其电池器件在50 mW/cm2强度光照下,开路电压(Voc)为0.54 V,短路电流密度(Jsc)为5.39 mA/cm2,能量转换效率为2.060%。
A new metal grid anode made of silver, copper and nickel is reported. Using it as anode, P3HT （poly （3-hexylthiophene））： PCBM （[6, 6]-phenylC61-butyricacidmethylester） layer as active layer, flexible polymer solar cells were manufactured by spin-coating. Five different structures of solar cell devices were made by using the traditional Indium tin oxide （ITO） anode material or the new anode material. After comparison, it is found that the performances of the new anode material device is greatly improved, open circuit voltage of 0. 54 V, short circuit current density of 5. 39 mA/cm^2, and power conversion efficiency （PCE） of 2. 060% are achieved under 50 mw/cm^2illumination.
出处
《应用光学》
CAS
CSCD
北大核心
2010年第2期210-214,共5页
Journal of Applied Optics
基金
国家自然科学基金(No.60678006)
作者简介
作者简介：杨少鹏（1964-），男，河北省人，教授，主要从事OLED及有机太阳能电池器件研究工作。E-mail：spyang@hbu．edu．cn