摘要
以水溶性Ni盐溶液为前体,制备了Ni液溶胶催化剂。考察了Ni液溶胶催化剂和水溶性Ni催化剂在原料油中的分散状况,对催化渣油加氢裂化反应后2种催化剂的状态进行了SEM、XPS和激光粒度表征。结果表明,Ni液溶胶催化剂比水溶性Ni催化剂在原料油中分散颗粒度小,比表面积大,分散均匀。在催化渣油加氢裂化反应后,Ni液溶胶催化剂和水溶性Ni催化剂中的Ni元素主要以Ni2+的形式存在,S主要以S2+和S6+2种形式存在,Ni液溶胶催化剂在反应后无明显团聚现象。2种催化剂存在下渣油加氢裂化反应生焦数据表明,Ni液溶胶催化剂比水溶性Ni催化剂具有更高的抑制生焦活性。
The Ni colloidal sol catalyst and water-soluble Ni catalyst were synthesized, which were also symbolized by use of microscope, SEM, TEM, XPS and LS granularity analyzing apparatus after being used in the slurry bed hydrocracking of residua. It was indicated that the average particle size of the Ni colloidal sol catalyst was smaller but the surface area was bigger than those of water- soluble Ni catalyst. After catalytic hydrocracking of residue the element Ni in the two catalysts existed as Ni2＋ and the element S existed as S2＋ and S6＋ , and there was no particle agglomeration phenomenon in Ni colloidal sol catalyst. Compared with water-soluble Ni catalyst, the Ni colloidal sol catalyst could restrain coke forming more effectively.
出处
《石油学报（石油加工）》
EI
CAS
CSCD
北大核心
2009年第6期873-878,共6页
Acta Petrolei Sinica(Petroleum Processing Section)
基金
中国石油科技创新基金研究项目(2008D-5006-04-03)资助
关键词
悬浮床
镍
胶体
催化剂
加氢
slurry phase
nickel
colloidal sol
catalyst
hydrogenation
作者简介
通讯联系人：刘东，E—mail：ldongupc@vip．sina．com刘东（1972-），男，副教授，博士，从事渣油悬浮床加氢工艺与催化剂的研究；
郑甲兆（1971-），男，工程师，从事石油加工工艺的研究；
马魁菊（1978-），女，工程师，硕士，从事重油结构及深加工的研究；
王雪莉（1971-），女，讲师，硕士，从事计算化学的研究；
阙国和（1938-），男，教授，从事渣油悬浮床加氢工艺与加氢催化剂的研究。