摘要
利用混合酸和氨水对催化裂解法制备的碳纳米管进行纯化和表面改性,然后研究了纳米氧化锡包覆碳纳米管。光谱实验结果表明,经过混合酸纯化和氨水改性后,碳纳米管表面拥有丰富的羟基、羧基和氨基等官能团。电子显微图像显示,通过回流和煅烧处理能够将纳米氧化锡包覆在碳纳米管的表面上。
Multi-walled carbon nanotubes （MWNT） synthesized by the catalytic chemical vapour decomposition method （CVD） were purified and modified by acid mixture and ammonia at boiling. The nano tin oxide coating of MWNT was obtained from block tin and nitric acid. The result of spectral analysis illuminates that there are many carboxyl, hydroxyl and amino groups on the wall of MWNT after treated by the mixture of acid and ammonia. The electron microscope images show that the modified MWNTs could be coated by tin oxide nano-particles after refluxed and calcined.
出处
《稀有金属材料与工程》
SCIE
EI
CAS
CSCD
北大核心
2008年第5期883-886,共4页
Rare Metal Materials and Engineering
基金
国家自然科学基金(No.50372020
59972031)
湖南省自然科学基金(No.01JJY2052)
湖南大学重大课题基金资助项目
关键词
碳纳米管
纳米氧化锡
表面改性
包覆
carbon nanotubes
nano tin oxide
surface modification
coating
作者简介
易斌，男，1982年生，硕士生，湖南大学材料科学与工程学院，湖南长沙410082，电话：0731-8641291，E-mail：enyage@sohu．com