摘要
利用短时研磨(粗磨,2 h)和长时研磨(细磨,48 h)两种不同的研磨工艺并结合B位复合陶瓷制备的一步法工艺流程,制备并研究了铅基钙钛矿弛豫铁电陶瓷(1-x)Pb(Ta0.5Sc0.5)O3-xPb(Zr0.52Ti0.48)O3(0.1≤x≤0.5)(PSTZT)。由细磨工艺制备的陶瓷在1 200℃下烧结2 h获得了纯钙钛矿相;细磨工艺PSTZT陶瓷表面平整、晶粒细小、致密性高,其介电与压电性能、热释电性能等全面优于粗磨工艺陶瓷。
The milling of ceramic materials is important in ceramics preparation and affects greatly the properties of prepared ceramics. Short time milling （2 h） and long time milling （48 h） are used in one-step-sintering method （OSSM） of preparation for complex ceramics at B site to prepare and investigate Pb-base Perovskite relaxor ferroelectric ceramics （1-x）Pb（Ta0.5Sc0.5）O3-xPb（Zr0.52Ti0.48）O3（0.1≤x≤0.5） （PSTZT）. The PSTZT obtained by long time milling procedure is sintered at 1 200 ℃ for 2 hours, which presents good surfacing and compactability, with fine grain and pure perovskite crystalline. The PSTZT is better in dielectric, piezoelectricity and pyroelectricity than those of ceramics from short time milling procedure.
出处
《桂林工学院学报》
CAS
北大核心
2008年第1期74-77,共4页
Journal of Guilin University of Technology
基金
国家自然科学基金资助项目(60471044)
广西科学基金资助项目(桂科青20020034)
关键词
细磨工艺
PSTZT陶瓷
纯钙钛矿陶瓷
fine milling procedure
PSTZT ceramics
pure perovskite ceramics
作者简介
张雪峰（1965-），男，硕士，副教授，研究方向：材料学。
通讯作者：蓝德均，博士，副教授，E-mail：landejunpingwy1262@126．com。