采用溶液共混煅烧法于800℃制备了Ce0.8Sm0.2O1.9(简称SDC)粉体。XRD分析表明Sm3+离子完全固溶在CeO2中,形成单相立方萤石结构SDC,晶粒平均粒径在1—3μm。用此粉体成型后在1 450℃烧结4 h获得了91.9%的相对密度。该固体电解质在800℃的电导率为0.087 S.cm-1。
Ce0.8Sm0.2O1.9（SDC） was synthesized by calcination of mixed solution method. XRD patterns showed that SDC powders calcined at 800 ℃ had a cubic fluorite structure and the average grain size was between 1-3 μm. After sintered for 4 h at 1 450 ℃, the relative density was 91.9%. The conductivity of SDC solid electrolyte was 0. 087 S·cm^-1 at 800℃.