摘要
在室温条件下采用射频磁控溅射方法,在纯棉机织物表面沉积TiO2功能纳米结构层.利用原子力显微镜和X射线衍射仪分别分析其表面形貌和晶态结构,同时对负载纳米TiO2织物的抗菌性和耐洗性进行了初步研究.实验表明,在拟定的溅射工艺条件下,纯棉机织物表面沉积了晶粒较为均匀、粒径较小的锐钛矿型纳米TiO2功能结构层,这一功能层使负载织物呈现出优良的抗菌性能;同时负载织物具有良好的耐洗性,经30次洗涤后,其抗菌性能仍保持在很高的水平.
Nanoscale titanium dioxide （TiO2） functional films were deposited on the surface of cotton fabric by RF magnetron sputter coating process. The surface microstructure and morphology were characterized by Atomic Force Microscope （AFM） and X-ray diffraction （XRD）. The results showed that the nanoscale titanium dioxide deposited on the surface of the treated cotton fabrics is at different anastasia phase. The particles of titanium dioxide had diameters in nano meter and distributed uniformly on the surface of cotton fibers. It was found that the coated fabrics shows excellent antibacterial property, and after 30 launderings, the antibacterial activity still maintained at a high level.
出处
《江南大学学报（自然科学版）》
CAS
2007年第4期474-477,共4页
Joural of Jiangnan University (Natural Science Edition)
基金
教育部科学技术研究重点项目(106089)
关键词
射频磁控溅射
二氧化钛
棉织物
抗菌
radio frequency magnetron sputtering
titanium dioxide
cotton fabrics
antibacterial
作者简介
徐阳（1964-），男，江苏丹阳人，讲师，纺织工程专业博士研究生．
通讯联系人：魏取福（1964-），男，安徽巢湖人，教授，工学博士，博士生导师．主要从事功能纺织材料的物理与化学以及纳米结构纺织材料的研究．Email：qufu—wei@sina．com