摘要
A W-Mo-Si/SiC double-layer oxidation protective coating for carbon/carbon （C/C） composites was prepared by a two-step pack cementation technique. XRD （X-ray diffraction） and SEM （scanning electron microscopy）results show that the coating obtained by the first step pack cementation was a thin inner buffer layer of SiC with some cracks and pores, and a new phase of （WxMo1-x）Si2 appeared after the second step pack cementation. Oxidation test shows that, after oxidation in air at 1773 K for 175 h and thermal cycling between 1773 K and room temperature for 18 times, the weight loss of the W-Mo-Si/SiC coated C/C composites was only 2.06%. The oxidation protective failure of the W-Mo-Si/SiC coating was attributed to the formation of some penetrable cracks in the coating.
A W-Mo-Si/SiC double-layer oxidation protective coating for carbon/carbon （C/C） composites was prepared by a two-step pack cementation technique. XRD （X-ray diffraction） and SEM （scanning electron microscopy）results show that the coating obtained by the first step pack cementation was a thin inner buffer layer of SiC with some cracks and pores, and a new phase of （WxMo1-x）Si2 appeared after the second step pack cementation. Oxidation test shows that, after oxidation in air at 1773 K for 175 h and thermal cycling between 1773 K and room temperature for 18 times, the weight loss of the W-Mo-Si/SiC coated C/C composites was only 2.06%. The oxidation protective failure of the W-Mo-Si/SiC coating was attributed to the formation of some penetrable cracks in the coating.
作者简介
Prof., Ph.D., to whom correspondence should be addressed, E-mail： likezhi@nwpu.edu.cn.