研究不同等效应变幅下ZL101铝合金在多轴比例和非比例载荷下的低周疲劳行为,并用透射电镜观察合金的疲劳行为中的位错结构。结果表明:合金在两种加载方式下均表现为循环硬化;在非比例载荷下合金表现出附加强化,但程度不明显;合金的疲劳寿命随等效应变幅的增加而降低,合金在非比例加载下的疲劳寿命低于比例加载时的疲劳寿命。对位错结构的观察表明,随等效应变幅度的提高,合金的低周疲劳位错结构从交叉位错带转化为位错胞,合金在非比例加载下更易形成位错胞结构。
Multi-axial low cycle fatigue behavior of cast aluminum alloys ZL101 at different equivalent strain ranges under proportional and non-proportional loadings were studied, the dislocation substructures of ZL 101 were observed by TEM. The results show that the aluminum alloy shows cyclic hardening both under multi-axial proportional and non-proportional loadings, while the cyclic additional hardening is shown under non-proportional loading, but the level is low. The multi-axial fatigue life decreases as the equivalent strain amplitude increases under both of multi-axial loadings. The fatigue life under non-proportional loading is less than that under proportional loading at the same equivalent strain amplitude. The deformation substructure examination reveals that with increasing equivalent strain amplitude, the dislocation structure tends to change from cross dislocation bands to dislocation cells. It is easier to form dislocation ceils under non-proportional loading.
出处
《中国有色金属学报》
EI
CAS
CSCD
北大核心
2007年第6期916-921,共6页
The Chinese Journal of Nonferrous Metals
基金
国家自然科学基金资助项目(50371063)
教育部新世纪优秀人才支持计划基金资助项目(NCET-05-0388)
牵引力国家重点实验室开放课题基金资助项目(TPL0501)
关键词
ZL101铝合金
多轴低周疲劳
非比例载荷
循环硬化
位错
cast aluminum alloys ZL101
multi-axial low cycle fatigue
non-proportional loading
cyclic hardening
dislocation
作者简介
通讯作者：朱正宇，博士：电话：021-65982463；E-mail：julien_yu@hotmail.com