为了更好地分析半固态镁合金的金相组织,应用VC++开发出半固态合金金相组织图片的定量分析系统,此系统能够有效分析半固态合金金相组织中的固相率、有效固相率、圆整度、颗粒尺寸及其等级等特征参数,并能对相连的固相颗粒进行有效识别。将此软件用于分析半固态镁合金试样的金相组织,对金相组织中固相颗粒的组分、形貌、大小等进行了描述,较好地评定了半固态合金金相组织的特征信息。经该定量分析系统测定的参数与目测结果基本一致。
The quantitative analysis system has been developed by VC software to analyze the microstructure of semi-solid magnesium alloy, which can effectively investigate the solid fraction, used solid fraction, roundness, particle size and its grade level of the microstructure, and identify the inter-connection solid particle. The microstructure of semi-solid magnesium alloy prepared by thixoforming and SIMA has been described by the software, including the content, morphology, size of solid particle in the microstructure, providing an excellent method for obtaining the feature information of semi-solid microstructure, which is well in agreement with the results of eyeballing.
出处
《特种铸造及有色合金》
CAS
CSCD
北大核心
2007年第5期369-372,共4页
Special Casting & Nonferrous Alloys
基金
国家高技术研究发展计划(863计划)资助项目(2002AA001022)
吉林省科技发展计划项目(20030503-1)
吉林大学"985工程"项目
关键词
半固态
组织
定量金相
固相率
Semi-solid, Microstructure, Quantitative Metallography, Solid Fraction
作者简介
张友法，男，1981年出生，博士研究生，吉林大学材料科学与工程学院，汽车材料教育部重点实验室，长春（130022），电话：0431-85095874，E-mail：zhangyoufa@email．jlu．edu．cn
通讯作者：曹占义，男，教授，吉林大学材料科学与工程学院，汽车材料教育部重点实验室，长春（130022），电话：0431-85095874，E-mail：caozy@jlu．edu．cn