在分析超磁致伸缩致动器热变形影响的基础上,结合实验论证,构建了在大电流、长时间且高精度场合下能对致动器进行整体温控的装置。设计并制作了一台超磁致伸缩致动器样机,在其电磁线圈的骨架中设置了内外两个水冷腔。通过恒温水的循环流动,带走线圈热量,以控制磁致伸缩棒和壳体的温度。进行了多组热变形对比实验,结果表明,致动器的整体温控装置有效地抑制了致动器的热变形影响,适合于大电流、高精度场合。
Based on theoretic analysis and experimental data, global temperature control of giant magne-tostrictive actuator（GMA） was proposed. A prototype of GMA was devised and manufactured, in which two cavities for water-cooling were set. One was for GMA rod and the other for shell. A measurement system for thermal deformation of GMA was presented. Comparative experiments on thermal deformation of GMA with water-cooling and without water-cooling were carried out. Experimental results show that the method of global temperature control of GMA presented can reduce thermal deformation of GMA greatly, especially, in the situation of large current and high accuracy.
出处
《中国机械工程》
EI
CAS
CSCD
北大核心
2007年第1期16-19,共4页
China Mechanical Engineering
基金
国家863高技术研究发展计划资助项目(2003AA414011)
湖北省自然科学基金资助项目(2005ABB023)
现代制造质量工程湖北省重点实验室开放基金资助重点项目(LMQ2006A01)
关键词
超磁致
致动器
热变形
温控
giant magnetostrictive
actuator
thermal deformation
temperature control
作者简介
卢全国，男，1976年生。武汉理工大学智能制造与控制研究所博士研究生，南昌工程学院机械与动力系讲师。主要研究方向为超磁致驱动与控制。发表论文12篇。
陈定方。男，1946年生。武汉理工大学智能制造与控制研究所教授、博士研究生导师。
钟毓宁，男，1965年生。湖北工业大学副校长，现代制造质量工程湖北省重点实验室教授。
陈敏，女，1982年生。武汉理工大学智能制造与控制研究所硕士研究生。