采用热力学计算法、扩散偶法以及差示扫描量热法(DSC)对Mg-B体系成相行为进行了研究。热力学计算显示,Mg-B体系固-固反应在298K^923K温度范围内均可以发生。扩散研究显示,Mg-B之间的固态反应是通过Mg向B扩散实现的。DSC研究表明,Mg-B体系在升温过程中,分别在527.12℃,650.73℃和660.82℃,先后发生了固-固反应,Mg熔化以及液-固反应。在综合考虑扩散研究、热力学研究结果的基础上,提出了Mg-B体系反应模型。
The behavior of the phase formation for the Mg-B system was investigated by thermodynamic calculation, couple diffusion and differential scanning calorimetry （DSC）. The result of thermodynamic calculation indicates that the solid-solid reaction for the Mg-B system will occur all in the temperature range from 298 K to 923 K. The results of diffusion experiment show that the solid reaction between Mg and B proceeds through Mg diffusing into B. The DSC research result indicates that the starting temperature of solid-solid reaction, Mg melting and liqiud-solid reaction is 527.12℃, 650.73℃ and 660.82℃, respectively. Based on the research results of diffusion and thermodynamic analysis, the reaction model of Mg-B system is proposed.
出处
《稀有金属材料与工程》
SCIE
EI
CAS
CSCD
北大核心
2006年第12期1892-1895,共4页
Rare Metal Materials and Engineering
基金
国家自然科学基金(50472099)
国家重点基础项目研究发展计划(2006CB601004)
西北工业大学博士论文创新基金
作者简介
闫世成，男，1979年生，博士生，西北工业大学材料学院，陕西西安710072。电话：029-86231079，E-mail：yscfei@tom.com