合成锂离子电池新型电解质锂盐L iBOB,并与PC/DEC溶剂配成电解液.室温下研究了L iBOB-PC/DEC电解液电导率随锂盐浓度的变化规律及其用于L i/ARG电池充放电循环性能的最佳组成配比,为0.5mol.L-1L iBOB-PC/DEC(3∶7).应用交流阻抗和循环伏安法研究了该最佳电解液的电化学性质及其电极/界面状态,结果显示,石墨电极在这种电解液中可形成良好的SEI膜.
The new electrolyte salt LiBOB for Li-ion battery was synthesized in laboratory, and series of electrolytes of LiBOB and PC/DEC was compounded. The conductivity of the electrolytes was compared by changing the temperature and concentration. The cyeling performance of charging-discharging was also compared by the charging-discharging test, the results showed that the varying regularity of conductivities and cycling stability and capacity were not always identical, but there were a suitable electrolyte for Li/ARG cell. The A. C. impedance and CV were used to test the compatibility of the most suitable electrolyte and ARG anode. Conclusion can be drawn that the ARG anode can be protected very well by SEI film in 0.5 mol·L^-1LiBOB-PC/DEC （3： 7）.
出处
《电化学》
CAS
CSCD
北大核心
2006年第3期257-261,共5页
Journal of Electrochemistry
基金
国家自然科学基金(50472093)资助
作者简介
通讯作者，Tel：（86．10）62332570，E-mail：lifsh_ustb@163．com