摘要
考察了瓜胶(GG)、丙烯酸(AA)的起始加料量和溶胀介质pH对瓜胶/聚丙烯酸半互穿网络水凝胶溶胀机理及溶胀动力学的影响。结果表明:在pH=3.0时,将GG用量从0增加到25 g/L,最大溶胀率从9.93下降到2.83,对应的溶胀特征指数n由0.600减小到0.203,水的扩散趋于F ick ian模式;将AA用量从125 g/L增加到375 g/L,最大溶胀率从3.14增加到4.30,n从0.484增加到0.609,水的扩散趋于non-F ick ian模式;GG/PAA半互穿网络水凝胶的溶胀行为满足Schott二级动力学方程。将溶胀介质pH从3.0提高到7.4,水凝胶的溶胀率、扩散特征指数n均明显增加。因此调整GG、AA用量以及溶胀介质pH可改变体系的溶胀性能。
A process was developed to prepare pH-sensitive guar gum/poly （acrylic acid） （GG/ PAA） semi-interpenetrating polymer network hydrogels. The influence of feed composition and pH in the swelling medium on swelling dynamics was investigated. Results show- the maximum swelling ratio and diffusion exponent n of hydrogels decrease with the increase GG amount, but increase with enhanced AA amount and pH. The swelling processes follow Schott second order dynamic equation. GG/PAA semi-IPNs are expected to be good candidates for the carriers for colon- specific drug delivery system.
出处
《高分子材料科学与工程》
EI
CAS
CSCD
北大核心
2006年第2期177-180,共4页
Polymer Materials Science & Engineering
关键词
PH敏感
瓜胶
聚丙烯酸
水凝胶
溶胀动力学
pH-sensitive
guar gum
poly （acrylic acid）
hydrogels
swelling dynamics
作者简介
联系人：吴文辉