摘要
采用不同表面性质的气相法纳米二氧化硅,利用硅橡胶混炼胶界面结合橡胶来研究高温硫化硅橡胶补强作用的影响因素,并结合扫描电镜分析界面的作用形式.结果表明结合橡胶以纳米二氧化硅的网络结构为骨架,纳米二氧化硅粉体的结构性越高,形成的三维立体网络结构结合橡胶体越好,对硅橡胶制品的补强效果越好.气相法纳米二氧化硅粉体填加质量分数为0.26～0.29时,表面羟基个数在1.1～1.4之间,有效补强体积最大,补强效果也最好.
Factors affecting reinforcement of high temperature vulcanizates were investigated using interfacial bound rubber samples of silicon rubber reinforced by fumed silica nanoparticles with different surface properties. Its interfacial action was analyzed by field emission scanning electron micrographs. Network of SiO2 nanoparticles formed the framework of the three-dimensional structure of bound rubber; the best reinforcement for silicon rubber was achieved using SiO2 nanoparticles with the highest structural performance. The largest effective reinforcement volume and best reinforcement would be achieved with a SiO2 filler content of 0. 26-0. 29 （mass fraction） and/or 1. 1 to 1. 4 OH groups.
出处
《华东理工大学学报（自然科学版）》
EI
CAS
CSCD
北大核心
2006年第1期51-54,89,共5页
Journal of East China University of Science and Technology
基金
上海市基础研究重大项目(04DZ14002)
国家自然科学基金(20236020
20176009)
国家基础研究重大项目前期研究专项(2002CCA02200)
教育部重点项目(02159)
上海市重点实验室专项基金(04DZ05622
05DZ22302)
上海市纳米科技专项基金
关键词
硅橡胶
气相法白炭黑
纳米二氧化硅
结合橡胶
补强性能
silicone rubber
fumed silica
silica nanoparticle
bound rubber
reinforcement property
作者简介
何颖（1977-）,女,吉林人,讲师,博士,研究方向：气相二氧化硅补强硅橡胶性能及机理研究.
李春忠,通讯联系人E-mail：czli@ecust.edu.cn