用复合电沉积工艺制备了纳米和微米La2O3颗粒增强镍基复合镀层,在销盘式滑动磨损试验机上考察了复合镀层在干摩擦条件下的摩擦磨损性能,用扫描电子显微镜分析了其磨损机理。结果表明:在干摩擦条件下,纳米La2O3颗粒增强复合镀层的摩擦磨损性能明显优于微米La2O3颗粒增强复合镀层;纳米La2O3增强镍基复合镀层的磨损主要表现为轻微磨粒磨损特征,而微米La2O3增强镍基复合镀层的磨损机制为剥层磨损和磨粒磨损。
Nanometer and micrometer La2O3 particles reinforced Ni matrix composite coatings were produced by composite electrodeposition. The friction and wear properties of the composite coatings were investigated using a pin--on--disc sliding wear machine under dry friction conditions. The worn surfaces of Ni matrix composite coatings, reinforced with nanometer and micrometer La2O3 particles, were analyzed with a scanning electron microscope （SEM）. The results reveal that the wear mechanism of nanometer La2O3 particles reinforced Ni matrix composite coating is characterized by slight abrasive wear, while that of micrometer La2O3 particles reinforced Ni matrix composite coating is characteristic of delaminate wear and abrasive wear.
出处
《中国机械工程》
EI
CAS
CSCD
北大核心
2006年第3期311-314,共4页
China Mechanical Engineering
基金
清华大学摩擦学国家重点实验室开放基金资助项目(SKLT04-03)
河南省高校杰出科研人才创新工程项目(2004KYCX006)
河南省先进制造技术重点实验室基金资助项目
河南科技大学重大科学前期预研专项(2004ZD003)
关键词
镍基复合镀层
La2O3颗粒
摩擦磨损性能
电沉积
Ni matrix composite coating
La2O3 particle
friction and wear propertie
electrodeposity
作者简介
薛玉君，男，1971年生。河南科技大学机电工程学院副教授。研究方向为摩擦学、纳米材料和特种加工。发表论文27篇。
段明德，男，1966年生。河南科技大学机电工程学院副教授。
李济顺，男，1963年生。河南科技人学机电工程学院教授。
马伟，男，1955年生。河南科技大学机电工程学院教授。