用KMnO4和MnSO4水溶液作为原料,用液相沉淀法制备无定形α-MnO2·nH2O.对样品进行比表面积测定(BET)、XRD、SEM等测试.通过循环伏安法和恒流充放电测试研究了样品的电化学行为.合成的无定形α-MnO2·nH2O在0.5mol/L的Na2SO4电解液中,在0～0.9 V(vs.SCE)范围内,电流为10 mA,2 mV/s的扫描速度下的比电容可达126.4 F/g.无定形α-MnO2·nH2O是较好的超级电容器电极材料.
Amorphous α-MnO2·nH2O was synthesized with chemical coprecipitation method by using KMnO4 and MnSO4 aqueous solution as raw materials. The sample was characterized by BET, XRD and SEM. The electrochemical characteristics of the sample were characterized by CV and constant current charge-discharge tests. The specific capacitance of the amorphous α-MnO2·nH2O was 126.4 F/g in 0.5 mol/L Na2SO4 electrolyte at the scan rate of 2 mV/s,the current of 10 mA, in the range of 0～0.9 V （vs. SCE）. The amorphous α-MnO2·nH2O was an excellent electrode material for suoercaoaeitor.
出处
《电池》
CAS
CSCD
北大核心
2005年第6期437-439,共3页
Battery Bimonthly
基金
973项目(2002CB211800)
国家自然科学基金(20373058)
福建省科技项目(2003H044)
关键词
超级电容器
电极材料
二氧化锰
比容量
supercapacitor
electrode material
MnO2
specific capacity
作者简介
张琦（1983-），女，天津人，厦门大学化学化工学院博士生，研究方向：化学电源。
郑明森（1975-），男，福建人，厦门大学化学化工学院博士生，研究方向：贮能材料。
朱亚薇（1980-），女，河北人，厦门大学化学化工学院硕士生，研究方向：化学电源。
董全峰（1964-），男，河南人，厦门大学宝龙电池研究所研究员，研究方向：聚合物锂离子电池。
金明钢（1968-），男，重庆人，厦门大学宝龙电池研究所高级工程师，研究方向：电池和电化学。
詹亚丁（1952-），女，福建人，厦门大学化学化工学院实验师，研究方向：贮能材料。
林祖赓（1934-），男，福建人，厦门大学化学化工学院教授，博士生导师，研究方向：电池和电化学。