摘要
以FeCrAl合金薄片为载体,以LaAl1-xFexO3为活性组分,以Al2O3为过渡层,制备了LaAl1-xFexO3/Al2O3/FeCrAl金属基整体式催化剂,并用XRD和SEM等方法对催化剂的物相和形貌进行了表征,对催化剂上甲烷催化燃烧活性进行了评价.结果表明,催化剂物相中有LaAl1-xFexO3型钙钛矿及-αAl2O3和-γAl2O3;催化剂的颗粒小于2μm,并且颗粒的尺寸及形貌与LaAl1-xFexO3中的Fe/Al摩尔比有关;催化剂样品对甲烷催化燃烧活性的大小顺序为LaAl0.3Fe0.7O3/Al2O3/FeCrAl>LaFeO3/Al2O3/FeCrAl>LaAl0.5Fe0.5O3/Al2O3/FeCrAl>LaAl0.7Fe0.3O3/Al2O3/FeCrAl>LaAlO3/Al2O3/FeCrAl.
A series of LaAl1-xFexO3/Al2O3/FeCrAl catalyst samples were prepared and characterized by X-ray diffraction and scanning electron microscopy. The catalytic activity of the catalyst samples for methane combustion was evaluated. The results indicated that the surface phase structure was LaAl1-xFexO3 perovskite-type oxide, a-Al2O3 and γ-Al2O3. The surface particle shape and size of the catalyst samples varied with the molar ratio of Fe to Al. The catalytic activity of the catalyst samples for methane combustion wasLaAl1-xFexO3/Al2O3/FeCrAl〉LaFeO3/Al2O3/FeCrAl〉LaAl0.5Fe0.5O3/Al2O3/FeCrAl〉LaAl0.7Fe0.3O3/Al2O3/FeCrAl〉LaAlO3/Al2O3/FeCrAl.
出处
《催化学报》
SCIE
CAS
CSCD
北大核心
2005年第11期1017-1021,共5页
基金
国家自然科学基金重点基金(20136010)
国家自然科学基金(20376005)
高等学校博士学科点专项科研基金(20030010002)
中国石化集团公司基金(X502019)
北京化工大学青年教师科研基金(QN0301)资助项目
关键词
镧
铝
铁
复合氧化物
铁-铬-铝合金
整体式催化剂
甲烷
燃烧
lanthanum, aluminium, iron, composite oxide, iron-chromium-aluminium alloy, monolithic catalyst, methane, combustion
作者简介
陈能展，男，1979年生，硕士研究生．联系人：季生福．Tel：（010）64412054；E-mail：jisf@mail．buct．edu．cn．联系人：李成岳．Tel：（010）64436787：E-mail：licy@mail．buct．edu．cn．