摘要
对烧结法制备氟金云母系微晶玻璃的热处理工艺制度进行了系统的研究。研究结果表明 ,在晶化温度为 75 0℃ ,晶化时间为 2h的热处理制度下 ,微晶玻璃具有最高的抗折强度 ( 10 7.5MPa)
A series of tests has been carried out to study the heat treatment system of the glass-ceramics.It has been found that the best heat treatment is crystallizing at 750?℃ for 2 hours by analyzing the test result of the flexure strength and density.With this heat treatment method,the glass-ceramics of the highest flexure strength(107.5?MPa)are obtained.
出处
《陶瓷》
CAS
2004年第6期25-27,共3页
Ceramics