The feedstock based on the binder 65%PW-30%EVA-5%SA has the best general rheological properties for the 17-4PH stainless steel powder. The 17-4PH stainless steel compacts sintered at 1 380 ℃ for 90 min have the best mechanical properties and the good microstructure with homogeneously distributed pore structure and the moderate-sized grains. Whereas the compacts sintered for 60 min and 120 min show an inadequate and an over-sintered microstructure respectively. The compacts sintered at 1380 ℃ for 90 min have the density of 7.70 g/cm^3, the strength of 1 275 MPa, the elongation of 5%, and hardness of HRC36. With the increase of sintering temperature, the density, strength and hardness increase, while the elongation decreases. The 17-4PH stainless steel has good corrosion resistance, showing an activation-passivation polarization curve. But the passivation potential range is narrow and the spot corrosion potential is low, indicating a low anti-spot corrosive properties.
The feedstock based on the binder 65%PW-30%EVA-5%SA has the best general rheological properties for the 17-4PH stainless steel powder. The 17-4PH stainless steel compacts sintered at 1 380 ℃ for 90 min have the best mechanical properties and the good microstructure with homogeneously distributed pore structure and the moderate-sized grains. Whereas the compacts sintered for 60 min and 120 min show an inadequate and an over-sintered microstructure respectively. The compacts sintered at 1380 ℃ for 90 min have the density of 7.70 g/cm^3, the strength of 1 275 MPa, the elongation of 5%, and hardness of HRC36. With the increase of sintering temperature, the density, strength and hardness increase, while the elongation decreases. The 17-4PH stainless steel has good corrosion resistance, showing an activation-passivation polarization curve. But the passivation potential range is narrow and the spot corrosion potential is low, indicating a low anti-spot corrosive properties.
出处
《中国有色金属学会会刊：英文版》
CSCD
2004年第5期934-939,共6页
Transactions of Nonferrous Metals Society of China
基金
Project( 2 0 0 1AA3 3 70 5 0 )supportedbyNationalHi techResearchDevelopmentProgramofChina
project( 810 41)sup portedbytheHUOYin dongEducationFoundation
project( 2 0 0 13 5 )supportedbytheChineseNationalExcellentDissertationFoundation
关键词
不锈钢
流变学
机械性能
耐腐蚀性
注模工艺
17-4PH
metal injection molding(MIM)
rheological properties
mechanical properties
corrosive resistance
17-4PH stainless steel