The influence of additive Nd_2O_3 on varistor voltage and microstructure of ZnO varistor was studied,and its mechanism was proposed from theoretical analysis. The results show that the varistor voltage of ZnO varistor increases with the content of Nd_2O_3 in the range of 0～0.04 (%,mol fraction). However when the content of Nd_2O_3 is more than 0.04 (%,mol fraction),the varistor voltage of ZnO varistor decreases with the content increase. The microstructure analysis indicates that a small amount of new compound with Nd exists at ZnO grain boundary and hinders the movement of grain boundary,which decreases the size of ZnO grain and makes the grain size and distribution homogeneous,as a result,additive (Nd_2O_3) raises the varistor voltage of the varistor greatly.
The influence of additive Nd_2O_3 on varistor voltage and microstructure of ZnO varistor was studied,and its mechanism was proposed from theoretical analysis. The results show that the varistor voltage of ZnO varistor increases with the content of Nd_2O_3 in the range of 0～0.04 (%,mol fraction). However when the content of Nd_2O_3 is more than 0.04 (%,mol fraction),the varistor voltage of ZnO varistor decreases with the content increase. The microstructure analysis indicates that a small amount of new compound with Nd exists at ZnO grain boundary and hinders the movement of grain boundary,which decreases the size of ZnO grain and makes the grain size and distribution homogeneous,as a result,additive (Nd_2O_3) raises the varistor voltage of the varistor greatly.