摘要
The crystallization and thermal fatigue behavior of Zr41Ti14Cu12.5Ni10Be22.5 bulk amorphous alloys heated by laser pulses was investigated. The results showed that crystallization occurred even below the crystallization temperature Tx in a low cycle time. Cracks appearred before or after crystallization of the heated area in the sample. The crystallization degree increased with the heating temperature and cycles. An increase in the fatigue cracks number was also observed. The plastic deformation in the heated area of the sample surface occurred, and became more pronounced with cycles and heating temperature.
The crystallization and thermal fatigue behavior of Zr41Ti14Cu12.5Ni10Be22.5 bulk amorphous alloys heated by laser pulses was investigated. The results showed that crystallization occurred even below the crystallization temperature Tx in a low cycle time. Cracks appearred before or after crystallization of the heated area in the sample. The crystallization degree increased with the heating temperature and cycles. An increase in the fatigue cracks number was also observed. The plastic deformation in the heated area of the sample surface occurred, and became more pronounced with cycles and heating temperature.
作者
JING Qin, ZHAO Liang, YUAN Hui, ZHANG Bing, NIU RunBing, ZHANG Jin, LI Gong, MA MingZhen & LIU RiPing State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004, China
基金
supported by the National Natural Science Foundation of China (Grant Nos. 50731005, 50821001, 50944029 and 50774006)
SKPBRC (Grant Nos. 2010CB731604 and 2006CB605201)
PCSIRT (Grant No. IRT0650)