The phase behavior of a well-defined poly(methyl methacrylate)- b- polystyrene block copolymer was studied by transmission electron microscope. The results show that a microphase transition may have occurred in the copolymer film. A kind of lamellae and an ordered bicontinuous double-diamond morphology are observed clearly. The lamellar morphology reveals a larger period of about 400 nm.
The phase behavior of a well-defined poly(methyl methacrylate)- b- polystyrene block copolymer was studied by transmission electron microscope. The results show that a microphase transition may have occurred in the copolymer film. A kind of lamellae and an ordered bicontinuous double-diamond morphology are observed clearly. The lamellar morphology reveals a larger period of about 400 nm.