Phosphorylated chitins (P-chitins) as the additives of calcium phosphate cements (CPCs) were prepared by the phosphorylation of chitin with phosphorus pentoxide in methanesulfonic acid. Their physical properties and effects on CPCs from monocalcium phosphate monohydrate (MCPM) and calcium oxide (CaO) or dicalcium phosphate dihydrate (DCPD) and calcium hydroxide [Ca(OH)(2)] were investigated. Addition of P-chitin (M-w = 2.60 x 10(4); degree of substitution, DS = 0.68) to the liquid phase in amounts up to 3 wt.% for MCPM and CaO cements or 1.5 wt.% for DCPD and Ca(OH)(2) cements could enhance the mechanical strength considerably, while little influence on the setting time was observed. However, further addition of P-chitin will cause no setting.
Phosphorylated chitins (P-chitins) as the additives of calcium phosphate cements (CPCs) were prepared by the phosphorylation of chitin with phosphorus pentoxide in methanesulfonic acid. Their physical properties and effects on CPCs from monocalcium phosphate monohydrate (MCPM) and calcium oxide (CaO) or dicalcium phosphate dihydrate (DCPD) and calcium hydroxide [Ca(OH)(2)] were investigated. Addition of P-chitin (M-w = 2.60 x 10(4); degree of substitution, DS = 0.68) to the liquid phase in amounts up to 3 wt.% for MCPM and CaO cements or 1.5 wt.% for DCPD and Ca(OH)(2) cements could enhance the mechanical strength considerably, while little influence on the setting time was observed. However, further addition of P-chitin will cause no setting.
基金
The project was financially supported by the National Natural Science Foundation of China (No. 20174018).
作者简介
Corresponding author: Jian-biao Ma (马建标), E-mail: jbma@ nankai.edu.cn