摘要
制备了氟含量不同的CaO-SiO_(2)-Na_(2)O-CaF_(2)类保护渣系,测试并获得了熔融状态下的原位拉曼光谱,并基于团簇结构的解谱拟合对其进行解析。结果表明,随着CaF_(2)含量的增加,硅酸盐微结构单元种类和相对含量发生变化。Q_(2)和Q_(3)减少,Q_(0)增加,Q_(1)总体含量呈现波动。
A series of CaO-SiO_(2)-Na_(2)O-CaF_(2)slag systems with different fluorine content were prepared.The in situ Raman spectra of molten slag systems were measured and obtained.The results showed that the types and relative contents of silicate microstructure units changed with the increase of CaF_(2)content.Q_(2)and Q_(3)decrease,Q_(0)increases,and the overall content of Q_(1)fluctuates.
作者
徐培磊
尤静林
张福
唐晓辉
刘国鹏
苏东艳
XU Pei-lei;YOU Jing-lin;ZHANG Fu;TANG Xiao-hui;LIU Guo-peng;SU Dong-yan(State Key Laboratory of Advanced Special Steel&shanghai Key Laboratory of Advanced Ferrometallurgy&School of Materials Science and Engineering,Shanghai University,Shanghai 200444,China)
出处
《光谱学与光谱分析》
SCIE
EI
CAS
CSCD
北大核心
2023年第S01期243-244,共2页
Spectroscopy and Spectral Analysis
基金
国家自然科学基金项目(22003039,21773152)
上海市科学技术委员会项目(12520709200)
111引智项目(D17002)
中国博士后科学基金项目(2019M661460)
中央军委科技委173项目(2021-JCJQ-ZD-051-00-02)资助
关键词
拉曼光谱
定量分析
含氟保护渣
Raman spectroscopy
Quantitative analysis
Fluorine-containing slag
作者简介
徐培磊,1997年生,省部共建高品质特殊钢冶金与制备国家重点实验室(上海大学)硕士研究生;通讯作者:尤静林,e-mail:jlyou@163.com