Sr2MgSi2O7:Eu^2+,Dy^3+/光转换剂复合红色发光材料是光转换剂与Sr2MgSi2O7:Eu^2+,Dy^3+按一定质量比混合后经联合剂处理制成的一种长余辉发光材料,具备Sr2MgSi2O7:Eu^2+,Dy^3+的高亮度、稳定性好等优良特性的同时能发出红色光。分别采用硅烷偶联剂(KH560)、铝酸酯偶联剂(DL-411-A)、铝锆偶联剂(LD-139-3)及其复合偶联剂(A:硅烷与铝酸酯偶联剂复合;B:硅烷、铝酸酯与铝锆偶联剂复合)作为联合剂,制备该复合红色发光材料。探究不同偶联剂对发光性能的影响。利用扫描电子显微镜、X射线衍射仪、荧光光谱仪、余辉亮度仪对复合发光材料的表面形貌、物相结构及发光性能进行分析和表征。结果表明:3种不同偶联剂对复合发光材料的发红光性能均有提升作用,复合偶联剂的效果更佳。经复合偶联剂B掺入后,Sr2MgSi2O7:Eu^2+,Dy^3+表面变得粗糙,黏附着大量的光转换剂颗粒。样品在605 nm左右发射峰强度提高了1.89倍,同时在470 nm左右发射峰强度下降了72%;初始余辉亮度提高了1.86倍左右;色纯度提高了1.87倍左右。
Composite red luminescent material Sr2MgSi2O7:Eu^2+,Dy^3+/light conversion agent is a kind of long-afterglow luminescent material prepared with a light conversion agent and Sr2MgSi2O7:Eu^2+,Dy^3+at a certain mass ratio.This material has excellent characteristics(i.e.high brightness and good stability)of Sr2MgSi2O7:Eu^2+,Dy^3+.Also,it can emit a red light.In this paper,silane coupling agent(i.e.KH560),aluminate-coupling agent(i.e.DL-411-A),zircoaluminate coupling agent(i.e.LD-139-3)and their composite coupling agents(i.e.A:composite of silane coupling agent and aluminate coupling agent;B:composite of silane coupling agent,aluminate coupling agent and aluminum zirconium coupling agent)were used to prepare the composite red luminescent materials.The effects of coupling agent on the luminescence properties were investigated.The surface morphology,phase structure and luminescence properties of the composite luminescent materials were characterized by scanning electron microscope,X-ray diffractometer,fluorescence spectrometer and afterglow luminance meter.The results show that three coupling agent all can improve the luminescence performance of composite luminescent materials,and the composite coupling agent has a better effect.The surface of Sr2MgSi2O7:Eu^2+,Dy^3+becomes coarse and adheres to the massive light conversion agent particles when a composite coupling agent B is used.In this case,the emission peak intensity of the sample is increased by 1.89 times at 605 nm,but decreased by 72%at 470 nm,the initial afterglow brightness is increased by 1.86 times,and the color purity is enhanced by 1.87 times.
作者
郑刘斌
朱亚楠
葛明桥
ZHENG Liubin;ZHU Yanan;GE Mingqiao(College of Textile&Clothing,Jiangnan University,Wuxi 214122,Jiangsu,China;Key Laboratory of Eco-Textiles,Ministry of Education,Jiangnan University,Wuxi 214122,Jiangsu,China)
出处
《硅酸盐学报》
EI
CAS
CSCD
北大核心
2020年第4期463-469,共7页
Journal of The Chinese Ceramic Society
基金
江苏省自然科学基金资助项目(BK20171140)
中国博士后科学基金(2018M630521).
关键词
铝酸酯偶联剂
铝锆偶联剂
光转换剂
红色发光材料
硅酸镁锶
aluminate coupling agent
aluminum zirconium coupling agent
light conversion agent
red luminescent materials
magnesium silicate
作者简介
第一作者:郑刘斌(1994—),男,硕士研究生,E-mail:1964613676@qq.com,2018年9月至今,于江南大学攻读工程硕士学位。主要从事功能性纤维制造领域的研究。所在课题组研究方向包括:功能化纺织技术、纤维制品现代加工技术及清洁化生产、功能性纺织材料制备理论与技术、纤维资源综合利用;通信作者:葛明桥(1957—),男,博士,教授,E-mail:ge_mingqiao@126.com,1999年3月毕业于日本福井大学物质工学专业,获工学博士学位。现任江南大学纺织服装学院教授、博士生导师。兼任江苏省高等学校高级职务评审委员、江苏省工程系列高级职务评审委员、江苏省科技厅科研项目、科技进步奖咨询专家和评委、国家863新材料技术领域专家库专家、日本纤维机械学会会员、江苏省化纤学会副理事长。主要论著1部、在国内外期刊上发表文章100余篇、申请专利30余项。主持和参加国家级(或省部级)项目数16项;朱亚楠(1989—),男,博士,副教授,E-mail:m13205291995@163.com,2015年1月年毕业于江南大学,获工学博士学位。现任江南大学副教授,江苏省纺织工程学会化纤专业委员会秘书。主要研究方向为功能性纤维制造理论与技术。发表专业学术论文20余篇,其中SCI论文10多篇,申请发明专利5项,授权1项。