粉煤灰地质聚合物作为一种新型绿色建筑材料,能够提升资源利用率,减少二氧化碳排放。为探究粉煤灰地质聚合物外掺矿渣和氧化镁的最优配比,试验将32.5MPa砌筑水泥和矿渣以及氧化镁等材料混合,用氢氧化钠和水玻璃复合作为碱性激发剂制备混凝土。和粉煤灰地质聚合物中掺入矿渣和氧化镁进行对比,发现随着矿渣和氧化镁掺量的增加,粉煤灰地质聚合物的抗压强度变化明显。在粉煤灰地质聚合物中,当粉煤灰的质量与矿渣和氧化镁的总质量之比为3∶4,矿渣中钙含量和氧化镁中镁含量的质量之比为1∶1时,粉煤灰地质聚合物的抗压强度优于普通混凝土,粉煤灰地质聚合物28d强度比普通混凝土强度高出23.91%。
Fly ash geopolymer,a new green building material,can improve resource utilization and reduce carbon dioxide emission.To get the most appropriate ratio of fly ash geopolymer mixed with slag and magnesium oxide,the concretes were developed with alkaline activator prepared by 32.5MPa masonry cement,slag and magnesium oxide.It is found that the compressive strength of geopolymer with fly ash changes more obviously with the increase of the content of slag and magnesium oxide.The compressive strength of fly ash geopolymer cured for 28d than normal concrete strength increased by 23.91%than that of ordinary concrete,when the quality ratio of fly ash to the total mass slag and of magnesium oxide is 3∶4,among them,ratio of calcium to magnesium of magnesium oxide in slag is 1∶1.
作者
吴新燕
沈杨海
陈羚
杨锦
WU Xinyan;SHEN Yanghai;CHEN Ling;YANG Jin(Jiyang College of Zhejiang A&F University,Zhuji 311800,China)
出处
《建筑结构》
CSCD
北大核心
2022年第S01期1604-1608,共5页
Building Structure
基金
浙江省基础研究项目(LGF18E080006)
2021年国家级大学生创新创业训练计划项目(202113283006)
关键词
地质聚合物
氧化镁
氧化钙
裂缝
抗压强度
geopolymer
Magnesium oxide
Calcium oxide
fissure
compressive strength
作者简介
第一作者:吴新燕,博士,高级工程师,Email:xinyan@zju.edu.cn;通信作者:沈杨海,学士,Email:shenyanghai2021@163.com。