In blue quantum dot light emitting diodes(QLEDs),electron injection is insufficient,which would degrade device efficiency and stability.Herein,we employ chlorine passivated ZnO nanoparticles as electron transport laye...In blue quantum dot light emitting diodes(QLEDs),electron injection is insufficient,which would degrade device efficiency and stability.Herein,we employ chlorine passivated ZnO nanoparticles as electron transport layer to facilitate electron injection into QDs effectively.Moreover,it suppresses exciton quenching at the QD/ZnO interface by blocking charge transfer channel.As a result,the maximum external quantum efficiency of blue QLED was increased from 2.55%to 4.60%,and the operation lifetime of blue QLED was nearly 4 times longer than that of the control device.Our work indicates that election injection plays an important role in blue QLED efficiency and stability.展开更多
Colloidal Pb Se nanocrystals(NCs)have gained considerable attention due to their efficient carrier multiplication and emissions across near-infrared and short-wavelength infrared spectral ranges.However,the fast degra...Colloidal Pb Se nanocrystals(NCs)have gained considerable attention due to their efficient carrier multiplication and emissions across near-infrared and short-wavelength infrared spectral ranges.However,the fast degradation of colloidal Pb Se NCs in ambient conditions hampers their widespread applications in infrared optoelectronics.It is well-known that the inorganic thick-shell over core improves the stability of NCs.Here,we present the synthesis of Pb Se/Pb S core/shell NCs showing wide spectral tunability,in which the molar ratio of lead(Pb)and sulfur(S)precursors,and the concentration of sulfur and Pb Se NCs in solvent have a significant effect on the efficient Pb S shell growth.The infrared light-emitting diodes(IR-LEDs)fabricated with the Pb Se/Pb S core/shell NCs exhibit an external quantum efficiency(EQE)of 1.3%at 1280 nm.The ligand exchange to optimize the distance between NCs and chloride treatment are important processes for achieving high performance on Pb Se/Pb S NC-LEDs.Our results provide evidence for the promising potential of Pb Se/Pb S NCs over the wide range of infrared optoelectronic applications.展开更多
基金Project supported by the National Key R&D Program of China(Grant Nos.2016YFB0401702 and 2017YFE0120400)the National Natural Science Foundation of China(Grant Nos.62005114,62005115,and 61875082)+5 种基金Key-Area Research and Development Program of Guangdong Province,China(Grant Nos.2019B010925001 and 2019B010924001)Guangdong University Key Laboratory for Advanced Quantum Dot Displays and Lighting(Grant No.2017KSYS007)Natural Science Foundation of Guangdong Province,China(Grant No.2017B030306010)Guangdong Basic and Applied Basic Research Foundation,China(Grant No.2019A1515110437)Shenzhen Peacock Team Project(Grant No.KQTD2016030111203005)High Level University Fund of Guangdong Province,China(Grant No.G02236004).
文摘In blue quantum dot light emitting diodes(QLEDs),electron injection is insufficient,which would degrade device efficiency and stability.Herein,we employ chlorine passivated ZnO nanoparticles as electron transport layer to facilitate electron injection into QDs effectively.Moreover,it suppresses exciton quenching at the QD/ZnO interface by blocking charge transfer channel.As a result,the maximum external quantum efficiency of blue QLED was increased from 2.55%to 4.60%,and the operation lifetime of blue QLED was nearly 4 times longer than that of the control device.Our work indicates that election injection plays an important role in blue QLED efficiency and stability.
基金Project supported by the National Key Research and Development Program of China(Grant No.2016YFB0401702)the National Natural Science Foundation of China(Grant Nos.61674074 and 61405089)+6 种基金Development and Reform Commission of Shenzhen Project,China(Grant No.[2017]1395)Shenzhen Peacock Team Project,China(Grant No.KQTD2016030111203005)Shenzhen Key Laboratory for Advanced Quantum Dot Displays and Lighting,China(Grant No.ZDSYS201707281632549)Guangdong Province’s Key R&D Program:Micro-LED Display and Ultra-high Brightness Micro-display Technology,China(Grant No.2019B010925001)Guangdong University Key Laboratory for Advanced Quantum Dot Displays and Lighting,China(Grant No.2017KSYS007)Distinguished Young Scholar of National Natural Science Foundation of Guangdong,China(Grant No.2017B030306010)the start-up fund from Southern University of Science and Technology,Shenzhen,China
文摘Colloidal Pb Se nanocrystals(NCs)have gained considerable attention due to their efficient carrier multiplication and emissions across near-infrared and short-wavelength infrared spectral ranges.However,the fast degradation of colloidal Pb Se NCs in ambient conditions hampers their widespread applications in infrared optoelectronics.It is well-known that the inorganic thick-shell over core improves the stability of NCs.Here,we present the synthesis of Pb Se/Pb S core/shell NCs showing wide spectral tunability,in which the molar ratio of lead(Pb)and sulfur(S)precursors,and the concentration of sulfur and Pb Se NCs in solvent have a significant effect on the efficient Pb S shell growth.The infrared light-emitting diodes(IR-LEDs)fabricated with the Pb Se/Pb S core/shell NCs exhibit an external quantum efficiency(EQE)of 1.3%at 1280 nm.The ligand exchange to optimize the distance between NCs and chloride treatment are important processes for achieving high performance on Pb Se/Pb S NC-LEDs.Our results provide evidence for the promising potential of Pb Se/Pb S NCs over the wide range of infrared optoelectronic applications.