CrTiAIN coatings were prepared by using a home-made industrial scale multi-arc ion plating system. The coatings were found to be composites of face-center-cubic CrN and TiN. The surface roughness, microhardness, and t...CrTiAIN coatings were prepared by using a home-made industrial scale multi-arc ion plating system. The coatings were found to be composites of face-center-cubic CrN and TiN. The surface roughness, microhardness, and tribological properties of the films were significantly affected by the nitrogen pressure and dc-pulsed bias voltage applied to the substrate. The CrTiA1N coatings with the smoothest surfaces were obtained at optimum conditions of nitrogen pressure of 5.0 Pa and bias voltage of -200 V. The samples were found to exhibit a hardness of 2900 HV0.05 with an average friction coefficient of 0.16 and wear rate of 1.5× 10^-16 m^3/N.m against cemented carbide.展开更多
基金supported by the China Ministry of Industry and Information Technology (No. 2009ZX04012-032)Basic Research Fund of Central Universities
文摘CrTiAIN coatings were prepared by using a home-made industrial scale multi-arc ion plating system. The coatings were found to be composites of face-center-cubic CrN and TiN. The surface roughness, microhardness, and tribological properties of the films were significantly affected by the nitrogen pressure and dc-pulsed bias voltage applied to the substrate. The CrTiA1N coatings with the smoothest surfaces were obtained at optimum conditions of nitrogen pressure of 5.0 Pa and bias voltage of -200 V. The samples were found to exhibit a hardness of 2900 HV0.05 with an average friction coefficient of 0.16 and wear rate of 1.5× 10^-16 m^3/N.m against cemented carbide.