Taking the saline lake bischofite and NH4Cl that was removed with the ammonia method and continuously followed by filtration as raw materials with a molar ratio of 1∶1 of MgCl2 to NH4Cl, ammonium carnallite was synth...Taking the saline lake bischofite and NH4Cl that was removed with the ammonia method and continuously followed by filtration as raw materials with a molar ratio of 1∶1 of MgCl2 to NH4Cl, ammonium carnallite was synthesized. And then the ammonium carnallite was dehydrated to some extent at 160℃ for 4 h. Ammonium carnallite reacted with ammonia at 240℃ for 150 min and the ammonation ammonium carnallite was produced. Finally, the ammonation ammonium carnallite was calcined at 750℃ into anhydrous magnesium chloride containing only 0.1%（mass fraction） of MgO. On the other hand, dehydrated ammonium carnallite was mixed with the solid ammonium chloride at mass ratio 1∶4 at high temperature and with the differential pressure of NH3 above 30.5kPa. The dehydrated ammonium carnallite of mixture was dehydrated at 410℃, and then calcined at 700℃ into anhydrous magnesium chloride with only 0.087%（mass fraction） of MgO. X-ray diffraction and electron microscopy analysis results prove that anhydrous magnesium chloride obtained by both methods hasn’t mixed phases, the particle is large and even has good dispersion, which is suitable for preparation of metal magnesium in the electrolysis.展开更多
Large and uniform tetrapod-like ZnO whiskers （T-ZnO） were prepared from waste hot dipping zinc by vapor oxidation and examined by means of X-ray diffraction and ICP-AES analysis and scanning electron microscope. The...Large and uniform tetrapod-like ZnO whiskers （T-ZnO） were prepared from waste hot dipping zinc by vapor oxidation and examined by means of X-ray diffraction and ICP-AES analysis and scanning electron microscope. The products are pure hexagonal wurtzite crystals with tetrapod shape and edge size of center body 56 μm and needle length of 100130 μm. The size and shape of ZnO particles are fully controlled by the growth conditions and T-ZnO can be obtained only at 8501 000 ℃ and total gas flow rate ranging from 40 to 250 L·h-1 in which the size of the T-ZnO particles varies slightly with temperature. The process of the formation of T-ZnO is that T-ZnO may nucleate at the initial stage with a complete tetrapod shape and develop to the large size, but not the process of （preferential） growth of octahedral nuclei and subsequent growth of the needles. The experiment presents a new method to prepare T-ZnO economically by using the waste hot dipping zinc.展开更多
基金Project(2000 G 101) supported by the Key Science and Technology Research Project of Qinghai Province
文摘Taking the saline lake bischofite and NH4Cl that was removed with the ammonia method and continuously followed by filtration as raw materials with a molar ratio of 1∶1 of MgCl2 to NH4Cl, ammonium carnallite was synthesized. And then the ammonium carnallite was dehydrated to some extent at 160℃ for 4 h. Ammonium carnallite reacted with ammonia at 240℃ for 150 min and the ammonation ammonium carnallite was produced. Finally, the ammonation ammonium carnallite was calcined at 750℃ into anhydrous magnesium chloride containing only 0.1%（mass fraction） of MgO. On the other hand, dehydrated ammonium carnallite was mixed with the solid ammonium chloride at mass ratio 1∶4 at high temperature and with the differential pressure of NH3 above 30.5kPa. The dehydrated ammonium carnallite of mixture was dehydrated at 410℃, and then calcined at 700℃ into anhydrous magnesium chloride with only 0.087%（mass fraction） of MgO. X-ray diffraction and electron microscopy analysis results prove that anhydrous magnesium chloride obtained by both methods hasn’t mixed phases, the particle is large and even has good dispersion, which is suitable for preparation of metal magnesium in the electrolysis.
文摘Large and uniform tetrapod-like ZnO whiskers （T-ZnO） were prepared from waste hot dipping zinc by vapor oxidation and examined by means of X-ray diffraction and ICP-AES analysis and scanning electron microscope. The products are pure hexagonal wurtzite crystals with tetrapod shape and edge size of center body 56 μm and needle length of 100130 μm. The size and shape of ZnO particles are fully controlled by the growth conditions and T-ZnO can be obtained only at 8501 000 ℃ and total gas flow rate ranging from 40 to 250 L·h-1 in which the size of the T-ZnO particles varies slightly with temperature. The process of the formation of T-ZnO is that T-ZnO may nucleate at the initial stage with a complete tetrapod shape and develop to the large size, but not the process of （preferential） growth of octahedral nuclei and subsequent growth of the needles. The experiment presents a new method to prepare T-ZnO economically by using the waste hot dipping zinc.