Acid mine drainage（AMD） is one of the main reasons of slope instability in chemical mines with high sulfide. The pH values of the solution inside the mining pit decrease with the increasing of distance from ore body...Acid mine drainage（AMD） is one of the main reasons of slope instability in chemical mines with high sulfide. The pH values of the solution inside the mining pit decrease with the increasing of distance from ore body and vary from 1.2 to 4.6, according to the results of the water environmental investigation and the composition test of the slope sandstone in Xinqiao Pyrite Mine. Comparative experiments between original sandstone and AMD eroded sandstone samples show that after AMD erosion the uniaxial compressive strength and elastic modulus decrease by 30%-50% and 25%-45%, respectively, the cohesion and internal friction angle decrease obviously, and the Poisson ratio fluctuates between 0.20-0.29. The greater joints development, the higher residual stress after peak value, and the longer time to damage. Besides above, the reaction mechanism analysis of AMD eroded sandstone shows that the fillings in joints and fissures of sandstone are frequently decomposed and polyreacted, resulting in changes of interior molecule structure and fi＇amework composition, and decreases of cohesion and angle of internal friction between rock structure interfaces.展开更多
Five types of polyurea elastomers were synthesized by changing the isocyanate component and the mechanical properties of polyurea materials were measured. Fiber-reinforced cement boards(FRCB)strengthened by polyurea w...Five types of polyurea elastomers were synthesized by changing the isocyanate component and the mechanical properties of polyurea materials were measured. Fiber-reinforced cement boards(FRCB)strengthened by polyurea with different formulations were processed, and a series of experiments were carried out on the specimens with gas explosion devices. The results showed that the conventional mechanical properties of different types of polyureas had their own advantages. Based on the gas explosion overpressure criterion, the blast resistances of reinforced plates were quantitatively evaluated,and the best polyurea was selected to guide the formulation design. The three typical failure modes of polyurea-reinforced FRCBs were flexural, shear, and flexural-shear failure. Dynamic thermodynamics and shock wave spectral analysis revealed that the polyurea did not undergo a glass transition in the gas explosion tests but retained its elastic properties, allowing it to effectively wrap the fragments formed by the brittle substrates.展开更多
基金Project(50321402) supported by the National Science Fund for Innovative Research Groupproject(2004CB619206) supported by tMajor State Basic Research Development Program of Chinaproject (50325414) supported by the National Science Fund fDistinguished Young Scholars
文摘Acid mine drainage（AMD） is one of the main reasons of slope instability in chemical mines with high sulfide. The pH values of the solution inside the mining pit decrease with the increasing of distance from ore body and vary from 1.2 to 4.6, according to the results of the water environmental investigation and the composition test of the slope sandstone in Xinqiao Pyrite Mine. Comparative experiments between original sandstone and AMD eroded sandstone samples show that after AMD erosion the uniaxial compressive strength and elastic modulus decrease by 30%-50% and 25%-45%, respectively, the cohesion and internal friction angle decrease obviously, and the Poisson ratio fluctuates between 0.20-0.29. The greater joints development, the higher residual stress after peak value, and the longer time to damage. Besides above, the reaction mechanism analysis of AMD eroded sandstone shows that the fillings in joints and fissures of sandstone are frequently decomposed and polyreacted, resulting in changes of interior molecule structure and fi＇amework composition, and decreases of cohesion and angle of internal friction between rock structure interfaces.
基金funded by National Natural Science Foundation of China(No.12002392).
文摘Five types of polyurea elastomers were synthesized by changing the isocyanate component and the mechanical properties of polyurea materials were measured. Fiber-reinforced cement boards(FRCB)strengthened by polyurea with different formulations were processed, and a series of experiments were carried out on the specimens with gas explosion devices. The results showed that the conventional mechanical properties of different types of polyureas had their own advantages. Based on the gas explosion overpressure criterion, the blast resistances of reinforced plates were quantitatively evaluated,and the best polyurea was selected to guide the formulation design. The three typical failure modes of polyurea-reinforced FRCBs were flexural, shear, and flexural-shear failure. Dynamic thermodynamics and shock wave spectral analysis revealed that the polyurea did not undergo a glass transition in the gas explosion tests but retained its elastic properties, allowing it to effectively wrap the fragments formed by the brittle substrates.