In the present work,paraffin phase change material is used as quenchant for the heat treatment of 42CrMo4 alloy and compared with water,air,and CuO doped paraffin.The samples were prepared based on ASTM E 8M-98 standa...In the present work,paraffin phase change material is used as quenchant for the heat treatment of 42CrMo4 alloy and compared with water,air,and CuO doped paraffin.The samples were prepared based on ASTM E 8M-98 standard for tensile test and then heated up to 830°C,kept for 4 h in an electric resistance furnace and then quenched in the mentioned media.Elastic modulus,yield strength,ultimate tensile strength,elongation,and modulus of toughness were determined according to the obtained stress?strain curves.Moreover,the hardness and microstructural evolution were investigated after the heat treatment at different media.The samples quenched in paraffin and CuO-doped paraffin are higher in ultimate tensile strength(1439 and 1306 MPa,respectively)than those quenched in water(1190 MPa)and air(1010 MPa).The highest hardness,with a value of HV 552,belonged to the sample quenched in CuO-doped paraffin.The microstructural studies revealed that the non-tempered steel had a ferrite/pearlite microstructure,while by quenching in water,paraffin and CuO-doped paraffin,ferrite/martensite microstructures were achieved.It is also observed that using the air as quenchant resulted in a three-phase bainite/martensite/ferrite microstructure.展开更多
The effects of postweld heat treatment on the microstructure and metallurgical properties of a bronze–carbon steel(st37)explosively bonded interface were studied.Explosive welding was done under 1.5-and 2-mm standoff...The effects of postweld heat treatment on the microstructure and metallurgical properties of a bronze–carbon steel(st37)explosively bonded interface were studied.Explosive welding was done under 1.5-and 2-mm standoff distances and different conditions of explosive charge.Samples were postweld heat treated for 4 and 16 h in the furnace at 250°C and 500°C and then air cooled.Laboratory studies using optical microscopy,scanning electron microscopy,and microhardness testing were used to evaluate the welded samples.Microstructural examinations showed that by increasing the standoff distance and the explosive charge,the interface of bronze to steel became wavier.The microhardness test result showed that the hardness of the samples was higher near the joint interface compared with other areas because of the intensive plastic deformation,which was caused by the explosion force.The results show that increasing the heat treatment temperature and time caused the intermetallic compounds’layer thickness to increase,and,because of the higher diffusion of copper and tin,the iron amount in the intermetallic compounds decreased.Also,because of the increase in heat treatment temperature and time,internal stresses were released,and the interface hardness decreased.展开更多
The flotation of pure and natural carbonaceous iron ore samples in the oleate flotation system was investigated.Starch can depress hematite effectively in a wide pH range,but cannot depress siderite efficiently in neu...The flotation of pure and natural carbonaceous iron ore samples in the oleate flotation system was investigated.Starch can depress hematite effectively in a wide pH range,but cannot depress siderite efficiently in neutral conditions.The flotation recovery of pure hematite,siderite,and quartz in the oleate-starch-CaCl2 system is significantly different when the slurry pH varies from 4 to 12.A novel two-step flotation process was developed for the separation of iron concentrate from Donganshan carbonaceous iron ore through which the siderite concentrate is first recovered and the high quality hematite concentrates with relative high iron recovery can be obtained in the second step flotation.The siderite concentrate may be utilized directly or undergo further concentration steps to increase iron grade.展开更多
As clean energy,the microwave is commonly used to pretreat various ores.In this work,the microwave dielectric properties of limonitic laterite ore were measured by resonant cavity perturbation technique and the effect...As clean energy,the microwave is commonly used to pretreat various ores.In this work,the microwave dielectric properties of limonitic laterite ore were measured by resonant cavity perturbation technique and the effects from microwave were systematically investigated.Results indicated that limonitic laterite had high microwave absorbance.After microwave pretreatment,the microstructure of the laterite became less aggregated and more porous and the main phase transformed from goethite to hematite that improved leaching in nitric acid(1.2 kg HNO3/kg ore);Ni,Co,Fe,and Mg extraction ratios were 95.2%,98.1%,1.8%and 15%,respectively,after leaching for 60 min at 200°C and 500 r/min.Furthermore,in the process of goethite to hematite by microwave pretreatment,the nickel-containing mineral is activated,which makes nickel be leached easily.The leaching process has high Ni extraction ratio compared to that without microwave(82%)and conventional pretreatment(90.4%).Therefore,microwave pretreatment of limonitic laterite before nitric acid pressure leaching is an effective way to improve the selectivity and extraction of the leach.展开更多
Presence of different terms with various values can alter the thermal behavior of the nanofluids flow over porous surfaces.The aim of this research is to study the influence of nanoparticles volume fraction,nanopartic...Presence of different terms with various values can alter the thermal behavior of the nanofluids flow over porous surfaces.The aim of this research is to study the influence of nanoparticles volume fraction,nanoparticles type,suction or injection,the heat generation or absorption,the Eckert number,thermal and velocity slip parameters,and radiation on the velocity and temperature fields on the flow and heat transfer over a porous flat plate.Four different types of nanoparticles including metal nanoparticles (Cu),metal oxide nanoparticles (Al2O3) and carbon-based nanomaterials (MWCNTs and SWCNTs) which were dispersed in the water (as based fluid) are studied.The governing equations are converted into the ordinary differential equations using similarity solution and solved numerically by the RKF45 algorithm.The results of the simulations showed a contradiction with the results of other researchers who expressed that using nanoparticles with higher thermal conductivity and volume fraction led to increasing heat transfer rate in nanofluids;this study proves that,in some cases,boosting the volume fraction of nanoparticles has a potential to decrease the heat transfer rate due to significant changes in values of some parameters including radiation,heat generation,and viscous dissipation.展开更多
Similar friction welded joints of AA-7005 aluminum rods were fabricated using different combinations of process parameters such as friction pressure(1.0, 1.5 and 2.0 MPa) and friction time(10, 15 and 20 s). Interfacia...Similar friction welded joints of AA-7005 aluminum rods were fabricated using different combinations of process parameters such as friction pressure(1.0, 1.5 and 2.0 MPa) and friction time(10, 15 and 20 s). Interfacial microstructure and formation of intermetallic compounds at the joint interface were evaluated via scanning electron microscopy(SEM) equipped with energy dispersive spectrum(EDS), and optical microscopy(OM). Microstructural observations reveal the formation of intermetallic phases during the welding process which cannot be extruded from the interface. Theses phases influence the tensile strength of the resultant joints. From the tensile characteristics viewpoint, the greatest tensile strength value of 365 MPa is obtained at 1.5 MPa and 15 s. Finally, the role of microstructural features on tensile strength of resultant joints is discussed.展开更多
This study was done to evaluate the nugget zone(NZ)corrosion behavior of dissimilar copper/brass joints welded by friction stir lap welding(FSLW)in a solution of 0.015 mol/L borax(pH 9.3).To this end,dissimilar copper...This study was done to evaluate the nugget zone(NZ)corrosion behavior of dissimilar copper/brass joints welded by friction stir lap welding(FSLW)in a solution of 0.015 mol/L borax(pH 9.3).To this end,dissimilar copper/brass plates were welded with two dissimilar heat inputs(low and high)during the welding procedure.The high and low heat inputs were conducted with 710 r/min,16 mm/min and 450 r/min,25 mm/min,respectively.Using open circuit potential(OCP)measurements,electrochemical impedance spectroscopy(EIS)and Tafel polarization tests,the electrochemical behavior of the specimens in borate buffer solution was assessed.With the help of scanning electron microscope(SEM),the morphology of welded specimen surfaces was examined after immersion in the test solution.According to the results,the NZ grain size and resistance improvement reduced due to the nugget zone corrosion with a decreased heat input.The results obtained from Tafel polarization and EIS indicated the improved corrosion behavior of the welded specimen NZ with a decrease in the heat input during the welding process unlike the copper and brass metals.Furthermore,an increased heat input during the welding process shows a reduction in the conditions for forming the passive films with higher protection behavior.展开更多
The organic phase separated from the interfacial crud provided by Dexing copper mine in Jiangxi, China, was analyzed by combined gas chromatography-mass spectroscopy. The results show that many kinds of emphiphiles co...The organic phase separated from the interfacial crud provided by Dexing copper mine in Jiangxi, China, was analyzed by combined gas chromatography-mass spectroscopy. The results show that many kinds of emphiphiles containing such hydrophilic groups as carbonyl, carboxyl, sulphonyl or acylamine exist in organic phase. Conclusively, Lix984N would degrade gradually during a long-term contact with the acidic aqueous feed and strip reagents. Lix84 and nonylphenol as effective components of Lix984N degraded almost completely after long-term recycling. Lix984N degraded through such reactions as Beck.mann rearrange, hydrolysis and sulphofication. The degradation of Lix984N would deteriorate solvent extraction and disengagement performance, and result in a more stable interracial emulsion.展开更多
Diglycidyl 4,5-epoxy tetrahydro phthalate/methyl tetrahydrophthalic anhydride （TDE-85/MeTHPA） epoxy resin modified by polyurethane （PU） was prepared with 1,4-butanediol （1,4-BDO）, trimethylol propane （TMP） and...Diglycidyl 4,5-epoxy tetrahydro phthalate/methyl tetrahydrophthalic anhydride （TDE-85/MeTHPA） epoxy resin modified by polyurethane （PU） was prepared with 1,4-butanediol （1,4-BDO）, trimethylol propane （TMP） and polyurethane prepolymer synthesized by polypropylene glycol and toluene diisocynate. Chemical reaction and curing mechanism of this system were discussed by incorporating the results of infra spectrum analysis. The results indicate that the epoxy polymeric network I is obtained by the curing reaction between TDE-85 and MeTHPA, while the PU polymeric network II is obtained by the chain-extended and crosslinking reaction between 1,4-BDO, TMP and polyurethane prepolymer（PUP）. The graft chemical bonds are formed between polymer networks I and II that therefore increase the degree of blend and compatibility between epoxy polymer and PU.展开更多
The restoration mechanisms for static recrystallization of work-hardened austenite were investigated by using double-pass compression tests performed on medium-carbon steel containing chromium and molybdenum. The soft...The restoration mechanisms for static recrystallization of work-hardened austenite were investigated by using double-pass compression tests performed on medium-carbon steel containing chromium and molybdenum. The softening fraction was defined by 2% offset method. The results show that Avrami exponent of about 0.21 is insensitive to deformation temperature, indicating that the action of steel grade should be considered. The time of 50% recrystallization (t0.5) decreases noteworthily with the increase of deformation temperature. Apparent activation energy for static recrystallization of 195 kJ/mol, which is close to that of vanadium microalloyed steel, is obtained by calculating. The increasing trend of the driving force for recrystallization is opposite to that of the deformation temperature, which is attributed to the number of operative slip system increasing as temperature increasing.展开更多
Glasses based on ZnO-Bi_2O_3-B_2O_3 system are expected to be a new kind of sealing glasses because of their low melting temperature and other properties.In order to reveal the effect of B_2O_3 on the rheological beha...Glasses based on ZnO-Bi_2O_3-B_2O_3 system are expected to be a new kind of sealing glasses because of their low melting temperature and other properties.In order to reveal the effect of B_2O_3 on the rheological behavior of ZnO-Bi_2O_3-B_2O_3 system glass melt,the properties of viscosity,thermal expansion,fluxion property and wetting process between cylinder samples and stainless steel were investigated with the rotating crucible viscometer,dilato meter and high-temperature microscope.The structure of sintered glass samples was investigated with scanning electron microscope.The results show that the B_2O_3 content increasing in B_1-B_3 at the given temperature between 400 ℃ and 500 ℃ leads to the increasing of the sample viscosity.When the amount of B_2O_3 increases from 5.24%to 9.24%(mass fraction),the coefficients of thermal expansion of glass samples decrease smoothly from 10.94×10^(-6) to10.71×10^(-6) and 10.38×10^(-6) ℃^(-1) respectively.In the case of sealing temperature,its value increases from 453 ℃ to 494 ℃.ZnO-Bi_2O_3-B_2O_3 system low-melting glass powder sintering was with viscous liquid to participate,which could make the densification of glass sample more effective and more efficient.With the content of B_2O_3 increasing,the wetting angle between the glasses samples and stainless steel could also increase,and the resulting appropriate sealing temperature range is 460-490 ℃.展开更多
Commercial pure aluminum and galvanized carbon steel were lap-welded using the weld-brazing(WB)technique.Three types of aluminum filler materials(4043,4047,and 5356) were used for WB.The joint strength and intermetall...Commercial pure aluminum and galvanized carbon steel were lap-welded using the weld-brazing(WB)technique.Three types of aluminum filler materials(4043,4047,and 5356) were used for WB.The joint strength and intermetallic compounds at the interface of three series of samples were analyzed and compared.Depending on the Si content,a variety of ternary Al-Fe-Si intermetallic compounds(IMCs) such as Fe_(4)(Al,Si)_(13),Fe_(2) Al_(8) Si(τ_(5)),and Fe_(2) Al_(9) Si_(2)(τ_(6)) were formed at the interface.Mg element in 5356 filler material cannot contribute to the formation of Al-Fe intermetallic phases due to the positive mixing enthalpy of Mg-Fe.The presence of Mg enhances the hot cracking phenomenon near the Al-Fe intermetallic compound at the interface.Zn coating does not participate in intermetallic formation due to its evaporation during WB.It was concluded that the softening of the base metal in the heat-affected zone rather than the IMCs determines the joint efficiency.展开更多
Design and optimization of bushing at present mainly use the traditional experience method.The relevant research that adopts computer simulation to carry on the operation behavior of the bushing has appeared in recent...Design and optimization of bushing at present mainly use the traditional experience method.The relevant research that adopts computer simulation to carry on the operation behavior of the bushing has appeared in recent years.How to use the finite element method to research bushing was introduced in the article.Physics fields and many relevant parameters of one real bushing were calculated.Through the results of calculation,it indicate that the finite element method is very useful in bushing research of designing and optimizing.展开更多
Mesoporous carbon CMK-3 was synthesized by using SBA-15 silica mesoporous as hard template and characterized through nitrogen adsorption/desorption and low angle X-ray diffraction.As-prepared material with large pores...Mesoporous carbon CMK-3 was synthesized by using SBA-15 silica mesoporous as hard template and characterized through nitrogen adsorption/desorption and low angle X-ray diffraction.As-prepared material with large pores and high surface area was used to remove Orange G dye from aqueous solution.Adsorption experiments were carried out as batch studies at variety of contact times,pH,initial dye concentrations,temperatures and salt concentrations.Langmuir and Freundlich isotherm models were employed to simulate the equilibrium data of anionic dye.It was found that the equilibrium data were well represented by the Langmuir isotherm,yielding maximum monolayer adsorption capacity of 189 mg/g.Experimental data were analyzed using pseudo-first order and pseudo-second order kinetic models and obtained results indicated that kinetics followed a pseudo-second order equation.展开更多
In current research,the interactive effects of different parameters such as melt overheating temperature,the location of gating system and incorporation of the grain refiner in bar and micro-powder form on the mechani...In current research,the interactive effects of different parameters such as melt overheating temperature,the location of gating system and incorporation of the grain refiner in bar and micro-powder form on the mechanical and structural characteristics of commercially pure aluminium are examined.Results show that increasing the melt temperature as well as employing a gating system with higher heat transfer rate increases the ultimate tensile strength(UTS)of the pure aluminium by 7%.Also,the introduction of 2wt%Al–5Ti–1B grain refiner in bar form into the overheated melt enhances the UTS values by two times,while incorporating 2wt%Al–5Ti–1B grain refiner in micro-powder form leads to achieving 32%higher UTS compared to the samples with grain refiner in the bar form due to the elimination of Al3Ti brittle phase,as confirmed by XRD patterns and SEM fracture surface images.展开更多
In this study, a newly developed duplex coating method incorporating plasma carburization and CrN coating was applied to Ti-6Al-4V and its effects on the wear resistance and fatigue life were investigated. The carburi...In this study, a newly developed duplex coating method incorporating plasma carburization and CrN coating was applied to Ti-6Al-4V and its effects on the wear resistance and fatigue life were investigated. The carburized layer with approximately150 μm in depth and CrN coating film with 7.5 μm in thickness were formed after duplex coating. Hard carbide particles such as TiC And V4C3 were formed in the carburized layer. XRD diffraction pattern analysis revealed that CrN film had predominant [111] and [200] textures. The hardness （Hv） was significantly improved up to about 1960 after duplex coating while the hardness value of original Ti-6Al-4V was 402. The threshold load for the modification and/or failure of CrN coating was measured to be 32N using the acoustic emission technique. The wear resistance and fatigue life of duplex coated Ti-6Al-4V improved significantly compared to those of un-treated specimen. The enhanced wear resistance can be attributed to the excellent adhesion and improved hardness of CrN coating film for the duplex coated Ti-6Al-4V. The initiation of fatigue cracks is likely to be retarded by the presence of hard and strong layers on the surface, resulting in the enhanced fatigue life.展开更多
The uniform experiment design is an effective way of optimizing technology scheme for refining the grain size during multistage deformation. In this paper, it is adopted to evaluate the effect of each technology param...The uniform experiment design is an effective way of optimizing technology scheme for refining the grain size during multistage deformation. In this paper, it is adopted to evaluate the effect of each technology parameter on final grain size of AISI H13 hot work tool steel during multistage deformation. It has been verified that the technology scheme for refining the final grain size can be determined rapidly and efficiently with the aid of the uniform design. The results show that the deformation parameters and the intermission time after deformation of the first stage affect the final grain size remarkably. For AISI H13 hot work tool steel, the final grain size can be refined notably when deformation parameters for the first stage are set as follows: a deformation temperature range of 1?025 1?085 ℃; a true strain of above 0.26 and the interpass time between the first and the second stage of deformation less than 10 s.展开更多
This study investigated the effect of pre-friction surfacing heat treatment of consumable rods and heat input during friction surfacing on the microstructure,mechanical properties,and wear resistance of hypereutectic ...This study investigated the effect of pre-friction surfacing heat treatment of consumable rods and heat input during friction surfacing on the microstructure,mechanical properties,and wear resistance of hypereutectic Al-Si alloy deposited on a commercially pure aluminum substrate.The results show that regardless of the consumable rod’s heat treatment conditions,the coating’s efficiency has increased with the increase in heat input,so the coating efficiency increases by 20%and 30%in the solid solution-treated rod and the artificially aged rod,respectively.By increasing the heat input,the average grain size in the coating fabricated by solid solution-treated rod and artificially aged rod increased from 0.1 to 0.9μm and from 0.2 to 1.3μm,respectively.At constant heat input,the average hardness and wear resistance of the coating created in the solid solution-treated rod are lower than those of the artificially aged rod.By decreasing heat input,the wear loss in the coating fabricated by solid solution-treated rod and artificially aged rod decreased by 10%and 20%,respectively,reaching 0.1 and 0.03μg/m.展开更多
文摘In the present work,paraffin phase change material is used as quenchant for the heat treatment of 42CrMo4 alloy and compared with water,air,and CuO doped paraffin.The samples were prepared based on ASTM E 8M-98 standard for tensile test and then heated up to 830°C,kept for 4 h in an electric resistance furnace and then quenched in the mentioned media.Elastic modulus,yield strength,ultimate tensile strength,elongation,and modulus of toughness were determined according to the obtained stress?strain curves.Moreover,the hardness and microstructural evolution were investigated after the heat treatment at different media.The samples quenched in paraffin and CuO-doped paraffin are higher in ultimate tensile strength(1439 and 1306 MPa,respectively)than those quenched in water(1190 MPa)and air(1010 MPa).The highest hardness,with a value of HV 552,belonged to the sample quenched in CuO-doped paraffin.The microstructural studies revealed that the non-tempered steel had a ferrite/pearlite microstructure,while by quenching in water,paraffin and CuO-doped paraffin,ferrite/martensite microstructures were achieved.It is also observed that using the air as quenchant resulted in a three-phase bainite/martensite/ferrite microstructure.
文摘The effects of postweld heat treatment on the microstructure and metallurgical properties of a bronze–carbon steel(st37)explosively bonded interface were studied.Explosive welding was done under 1.5-and 2-mm standoff distances and different conditions of explosive charge.Samples were postweld heat treated for 4 and 16 h in the furnace at 250°C and 500°C and then air cooled.Laboratory studies using optical microscopy,scanning electron microscopy,and microhardness testing were used to evaluate the welded samples.Microstructural examinations showed that by increasing the standoff distance and the explosive charge,the interface of bronze to steel became wavier.The microhardness test result showed that the hardness of the samples was higher near the joint interface compared with other areas because of the intensive plastic deformation,which was caused by the explosion force.The results show that increasing the heat treatment temperature and time caused the intermetallic compounds’layer thickness to increase,and,because of the higher diffusion of copper and tin,the iron amount in the intermetallic compounds decreased.Also,because of the increase in heat treatment temperature and time,internal stresses were released,and the interface hardness decreased.
基金Project(2006DFB72570) supported by the Grand Project of International Cooperation of Ministry of Science and Technology of China
文摘The flotation of pure and natural carbonaceous iron ore samples in the oleate flotation system was investigated.Starch can depress hematite effectively in a wide pH range,but cannot depress siderite efficiently in neutral conditions.The flotation recovery of pure hematite,siderite,and quartz in the oleate-starch-CaCl2 system is significantly different when the slurry pH varies from 4 to 12.A novel two-step flotation process was developed for the separation of iron concentrate from Donganshan carbonaceous iron ore through which the siderite concentrate is first recovered and the high quality hematite concentrates with relative high iron recovery can be obtained in the second step flotation.The siderite concentrate may be utilized directly or undergo further concentration steps to increase iron grade.
基金Project(51974025)supported by the National Natural Science Foundation of ChinaProject(2018IA055)supported by the International Cooperation Project of Key Research and Development Plan of Yunan Province,ChinaProject(JKY2019-09)supported by State Key Laboratory of Nickel and Cobalt Resources Comprehensive Utilization,China。
文摘As clean energy,the microwave is commonly used to pretreat various ores.In this work,the microwave dielectric properties of limonitic laterite ore were measured by resonant cavity perturbation technique and the effects from microwave were systematically investigated.Results indicated that limonitic laterite had high microwave absorbance.After microwave pretreatment,the microstructure of the laterite became less aggregated and more porous and the main phase transformed from goethite to hematite that improved leaching in nitric acid(1.2 kg HNO3/kg ore);Ni,Co,Fe,and Mg extraction ratios were 95.2%,98.1%,1.8%and 15%,respectively,after leaching for 60 min at 200°C and 500 r/min.Furthermore,in the process of goethite to hematite by microwave pretreatment,the nickel-containing mineral is activated,which makes nickel be leached easily.The leaching process has high Ni extraction ratio compared to that without microwave(82%)and conventional pretreatment(90.4%).Therefore,microwave pretreatment of limonitic laterite before nitric acid pressure leaching is an effective way to improve the selectivity and extraction of the leach.
文摘Presence of different terms with various values can alter the thermal behavior of the nanofluids flow over porous surfaces.The aim of this research is to study the influence of nanoparticles volume fraction,nanoparticles type,suction or injection,the heat generation or absorption,the Eckert number,thermal and velocity slip parameters,and radiation on the velocity and temperature fields on the flow and heat transfer over a porous flat plate.Four different types of nanoparticles including metal nanoparticles (Cu),metal oxide nanoparticles (Al2O3) and carbon-based nanomaterials (MWCNTs and SWCNTs) which were dispersed in the water (as based fluid) are studied.The governing equations are converted into the ordinary differential equations using similarity solution and solved numerically by the RKF45 algorithm.The results of the simulations showed a contradiction with the results of other researchers who expressed that using nanoparticles with higher thermal conductivity and volume fraction led to increasing heat transfer rate in nanofluids;this study proves that,in some cases,boosting the volume fraction of nanoparticles has a potential to decrease the heat transfer rate due to significant changes in values of some parameters including radiation,heat generation,and viscous dissipation.
文摘Similar friction welded joints of AA-7005 aluminum rods were fabricated using different combinations of process parameters such as friction pressure(1.0, 1.5 and 2.0 MPa) and friction time(10, 15 and 20 s). Interfacial microstructure and formation of intermetallic compounds at the joint interface were evaluated via scanning electron microscopy(SEM) equipped with energy dispersive spectrum(EDS), and optical microscopy(OM). Microstructural observations reveal the formation of intermetallic phases during the welding process which cannot be extruded from the interface. Theses phases influence the tensile strength of the resultant joints. From the tensile characteristics viewpoint, the greatest tensile strength value of 365 MPa is obtained at 1.5 MPa and 15 s. Finally, the role of microstructural features on tensile strength of resultant joints is discussed.
文摘This study was done to evaluate the nugget zone(NZ)corrosion behavior of dissimilar copper/brass joints welded by friction stir lap welding(FSLW)in a solution of 0.015 mol/L borax(pH 9.3).To this end,dissimilar copper/brass plates were welded with two dissimilar heat inputs(low and high)during the welding procedure.The high and low heat inputs were conducted with 710 r/min,16 mm/min and 450 r/min,25 mm/min,respectively.Using open circuit potential(OCP)measurements,electrochemical impedance spectroscopy(EIS)and Tafel polarization tests,the electrochemical behavior of the specimens in borate buffer solution was assessed.With the help of scanning electron microscope(SEM),the morphology of welded specimen surfaces was examined after immersion in the test solution.According to the results,the NZ grain size and resistance improvement reduced due to the nugget zone corrosion with a decreased heat input.The results obtained from Tafel polarization and EIS indicated the improved corrosion behavior of the welded specimen NZ with a decrease in the heat input during the welding process unlike the copper and brass metals.Furthermore,an increased heat input during the welding process shows a reduction in the conditions for forming the passive films with higher protection behavior.
基金Project (P1502) supported by Shanghai Leading Academic Discipline
文摘The organic phase separated from the interfacial crud provided by Dexing copper mine in Jiangxi, China, was analyzed by combined gas chromatography-mass spectroscopy. The results show that many kinds of emphiphiles containing such hydrophilic groups as carbonyl, carboxyl, sulphonyl or acylamine exist in organic phase. Conclusively, Lix984N would degrade gradually during a long-term contact with the acidic aqueous feed and strip reagents. Lix84 and nonylphenol as effective components of Lix984N degraded almost completely after long-term recycling. Lix984N degraded through such reactions as Beck.mann rearrange, hydrolysis and sulphofication. The degradation of Lix984N would deteriorate solvent extraction and disengagement performance, and result in a more stable interracial emulsion.
基金Project(2003AA84ts04) supported by the National High-Tech Research and Development Program of China
文摘Diglycidyl 4,5-epoxy tetrahydro phthalate/methyl tetrahydrophthalic anhydride （TDE-85/MeTHPA） epoxy resin modified by polyurethane （PU） was prepared with 1,4-butanediol （1,4-BDO）, trimethylol propane （TMP） and polyurethane prepolymer synthesized by polypropylene glycol and toluene diisocynate. Chemical reaction and curing mechanism of this system were discussed by incorporating the results of infra spectrum analysis. The results indicate that the epoxy polymeric network I is obtained by the curing reaction between TDE-85 and MeTHPA, while the PU polymeric network II is obtained by the chain-extended and crosslinking reaction between 1,4-BDO, TMP and polyurethane prepolymer（PUP）. The graft chemical bonds are formed between polymer networks I and II that therefore increase the degree of blend and compatibility between epoxy polymer and PU.
文摘The restoration mechanisms for static recrystallization of work-hardened austenite were investigated by using double-pass compression tests performed on medium-carbon steel containing chromium and molybdenum. The softening fraction was defined by 2% offset method. The results show that Avrami exponent of about 0.21 is insensitive to deformation temperature, indicating that the action of steel grade should be considered. The time of 50% recrystallization (t0.5) decreases noteworthily with the increase of deformation temperature. Apparent activation energy for static recrystallization of 195 kJ/mol, which is close to that of vanadium microalloyed steel, is obtained by calculating. The increasing trend of the driving force for recrystallization is opposite to that of the deformation temperature, which is attributed to the number of operative slip system increasing as temperature increasing.
基金Project(2012BAA08B04)supported by the National“Twelfth Five-Year”Plan for Science&Technology Support of China
文摘Glasses based on ZnO-Bi_2O_3-B_2O_3 system are expected to be a new kind of sealing glasses because of their low melting temperature and other properties.In order to reveal the effect of B_2O_3 on the rheological behavior of ZnO-Bi_2O_3-B_2O_3 system glass melt,the properties of viscosity,thermal expansion,fluxion property and wetting process between cylinder samples and stainless steel were investigated with the rotating crucible viscometer,dilato meter and high-temperature microscope.The structure of sintered glass samples was investigated with scanning electron microscope.The results show that the B_2O_3 content increasing in B_1-B_3 at the given temperature between 400 ℃ and 500 ℃ leads to the increasing of the sample viscosity.When the amount of B_2O_3 increases from 5.24%to 9.24%(mass fraction),the coefficients of thermal expansion of glass samples decrease smoothly from 10.94×10^(-6) to10.71×10^(-6) and 10.38×10^(-6) ℃^(-1) respectively.In the case of sealing temperature,its value increases from 453 ℃ to 494 ℃.ZnO-Bi_2O_3-B_2O_3 system low-melting glass powder sintering was with viscous liquid to participate,which could make the densification of glass sample more effective and more efficient.With the content of B_2O_3 increasing,the wetting angle between the glasses samples and stainless steel could also increase,and the resulting appropriate sealing temperature range is 460-490 ℃.
基金Project(97.13966(97.11.15)) supported by the Deputy of Research and Technology of Arak University,Iran。
文摘Commercial pure aluminum and galvanized carbon steel were lap-welded using the weld-brazing(WB)technique.Three types of aluminum filler materials(4043,4047,and 5356) were used for WB.The joint strength and intermetallic compounds at the interface of three series of samples were analyzed and compared.Depending on the Si content,a variety of ternary Al-Fe-Si intermetallic compounds(IMCs) such as Fe_(4)(Al,Si)_(13),Fe_(2) Al_(8) Si(τ_(5)),and Fe_(2) Al_(9) Si_(2)(τ_(6)) were formed at the interface.Mg element in 5356 filler material cannot contribute to the formation of Al-Fe intermetallic phases due to the positive mixing enthalpy of Mg-Fe.The presence of Mg enhances the hot cracking phenomenon near the Al-Fe intermetallic compound at the interface.Zn coating does not participate in intermetallic formation due to its evaporation during WB.It was concluded that the softening of the base metal in the heat-affected zone rather than the IMCs determines the joint efficiency.
基金National Science Foundation of China Yunnan United Foundation.(U0837601)the Natural Science Foundation of Yunnan Province,China(2010CF126)
文摘Design and optimization of bushing at present mainly use the traditional experience method.The relevant research that adopts computer simulation to carry on the operation behavior of the bushing has appeared in recent years.How to use the finite element method to research bushing was introduced in the article.Physics fields and many relevant parameters of one real bushing were calculated.Through the results of calculation,it indicate that the finite element method is very useful in bushing research of designing and optimizing.
基金the research council of Science and Research campus of Islamic Azad University for the financial support
文摘Mesoporous carbon CMK-3 was synthesized by using SBA-15 silica mesoporous as hard template and characterized through nitrogen adsorption/desorption and low angle X-ray diffraction.As-prepared material with large pores and high surface area was used to remove Orange G dye from aqueous solution.Adsorption experiments were carried out as batch studies at variety of contact times,pH,initial dye concentrations,temperatures and salt concentrations.Langmuir and Freundlich isotherm models were employed to simulate the equilibrium data of anionic dye.It was found that the equilibrium data were well represented by the Langmuir isotherm,yielding maximum monolayer adsorption capacity of 189 mg/g.Experimental data were analyzed using pseudo-first order and pseudo-second order kinetic models and obtained results indicated that kinetics followed a pseudo-second order equation.
文摘In current research,the interactive effects of different parameters such as melt overheating temperature,the location of gating system and incorporation of the grain refiner in bar and micro-powder form on the mechanical and structural characteristics of commercially pure aluminium are examined.Results show that increasing the melt temperature as well as employing a gating system with higher heat transfer rate increases the ultimate tensile strength(UTS)of the pure aluminium by 7%.Also,the introduction of 2wt%Al–5Ti–1B grain refiner in bar form into the overheated melt enhances the UTS values by two times,while incorporating 2wt%Al–5Ti–1B grain refiner in micro-powder form leads to achieving 32%higher UTS compared to the samples with grain refiner in the bar form due to the elimination of Al3Ti brittle phase,as confirmed by XRD patterns and SEM fracture surface images.
文摘In this study, a newly developed duplex coating method incorporating plasma carburization and CrN coating was applied to Ti-6Al-4V and its effects on the wear resistance and fatigue life were investigated. The carburized layer with approximately150 μm in depth and CrN coating film with 7.5 μm in thickness were formed after duplex coating. Hard carbide particles such as TiC And V4C3 were formed in the carburized layer. XRD diffraction pattern analysis revealed that CrN film had predominant [111] and [200] textures. The hardness （Hv） was significantly improved up to about 1960 after duplex coating while the hardness value of original Ti-6Al-4V was 402. The threshold load for the modification and/or failure of CrN coating was measured to be 32N using the acoustic emission technique. The wear resistance and fatigue life of duplex coated Ti-6Al-4V improved significantly compared to those of un-treated specimen. The enhanced wear resistance can be attributed to the excellent adhesion and improved hardness of CrN coating film for the duplex coated Ti-6Al-4V. The initiation of fatigue cracks is likely to be retarded by the presence of hard and strong layers on the surface, resulting in the enhanced fatigue life.
基金TheNationalNaturalScienceFoundationofChina (No .5 0 0 75 0 5 3)
文摘The uniform experiment design is an effective way of optimizing technology scheme for refining the grain size during multistage deformation. In this paper, it is adopted to evaluate the effect of each technology parameter on final grain size of AISI H13 hot work tool steel during multistage deformation. It has been verified that the technology scheme for refining the final grain size can be determined rapidly and efficiently with the aid of the uniform design. The results show that the deformation parameters and the intermission time after deformation of the first stage affect the final grain size remarkably. For AISI H13 hot work tool steel, the final grain size can be refined notably when deformation parameters for the first stage are set as follows: a deformation temperature range of 1?025 1?085 ℃; a true strain of above 0.26 and the interpass time between the first and the second stage of deformation less than 10 s.
文摘This study investigated the effect of pre-friction surfacing heat treatment of consumable rods and heat input during friction surfacing on the microstructure,mechanical properties,and wear resistance of hypereutectic Al-Si alloy deposited on a commercially pure aluminum substrate.The results show that regardless of the consumable rod’s heat treatment conditions,the coating’s efficiency has increased with the increase in heat input,so the coating efficiency increases by 20%and 30%in the solid solution-treated rod and the artificially aged rod,respectively.By increasing the heat input,the average grain size in the coating fabricated by solid solution-treated rod and artificially aged rod increased from 0.1 to 0.9μm and from 0.2 to 1.3μm,respectively.At constant heat input,the average hardness and wear resistance of the coating created in the solid solution-treated rod are lower than those of the artificially aged rod.By decreasing heat input,the wear loss in the coating fabricated by solid solution-treated rod and artificially aged rod decreased by 10%and 20%,respectively,reaching 0.1 and 0.03μg/m.