Ni(OH)2 including 20%Al was synthesized by solid state reaction. The result of XRD indicated that the sample thus prepared was α Ni(OH)2, and its size and crystalline form were much poorer than those of the sample pr...Ni(OH)2 including 20%Al was synthesized by solid state reaction. The result of XRD indicated that the sample thus prepared was α Ni(OH)2, and its size and crystalline form were much poorer than those of the sample prepared by solution state reaction. TG and DTA curves showed that α Ni(OH)2 began to decompose at higher temperature than β Ni(OH)2. The electrochemical behaviorsof the sample were studied by cyclic voltammetry and constant current charge discharge experiment. It was found that the sample by solid state reaction hadmore excellent electrode reversibility, higher discharge potential and higher discharge capacity.展开更多
文摘Ni(OH)2 including 20%Al was synthesized by solid state reaction. The result of XRD indicated that the sample thus prepared was α Ni(OH)2, and its size and crystalline form were much poorer than those of the sample prepared by solution state reaction. TG and DTA curves showed that α Ni(OH)2 began to decompose at higher temperature than β Ni(OH)2. The electrochemical behaviorsof the sample were studied by cyclic voltammetry and constant current charge discharge experiment. It was found that the sample by solid state reaction hadmore excellent electrode reversibility, higher discharge potential and higher discharge capacity.