For evaluation of the rheological and mechanical properties of highly filled wood plastic composites （WPCs）, polypropylene/polyethylene （PP/PE） blends were grafted with maleic anhydride （MAH） to enhance the inte...For evaluation of the rheological and mechanical properties of highly filled wood plastic composites （WPCs）, polypropylene/polyethylene （PP/PE） blends were grafted with maleic anhydride （MAH） to enhance the interfacial adhesion between wood fiber and matrix. WPCs were prepared from wood fiber up to 60 wt.% and modified PP/PE was blended by extrusion. The rheological properties were studied by using dynamic measurement. According to the strain sweep test, the linear viscoelastic region of composites in the melt was determined. The result showed that the storage modulus was independent of the strain at low strain region （〈0.1%）. The frequency sweep resuits indicated that all composites exhibited shear thinning behavior, and both the storage modulus and complex viscosity of MAH modified composites were decreased comparing to those unmodified. Flexural properties and impact strength of the prepared WPCs were measured according to the relevant standard specifications. The flexural and impact strength of the manufactured composites significantly increased and reached a maximum when MAH dosage was 1.0 wt%, whereas the flexural modulus after an initial decreased, also increased with MAH dosage. The increase in mechanical properties indicated that the presence of anhydride groups enhanced the interracial adhesion between wood fiber and PP/PE blends.展开更多
The effect of maleic anhydride grafted styrene-ethylene- buty-lene-styrene block copolymer （SEBS-g-MAH） and in-situ grafting MAH on mechanical, dynamic mechanical properties of wood flour/recycled plastic blends com...The effect of maleic anhydride grafted styrene-ethylene- buty-lene-styrene block copolymer （SEBS-g-MAH） and in-situ grafting MAH on mechanical, dynamic mechanical properties of wood flour/recycled plastic blends composites was investigated. Recycled plastic polypro-pylene （PP）, high-density polyethylene （HDPE） and polystyrene （PS）, were mixed with wood flour in a high speed blender and then extruded by a twin/single screw tandem extruder system to form wood flour/recycled plastic blends composites. Results show that the impact properties of the composites were improved more significantly by using SEBS-g-MAH compatibilizer than by using the mixtures of MAH and DCP via reactive blending in situ. However, contrary results were ob-served on the tensile and flexural properties of the corresponding com-posites. In General, the mechanical properties of composites made from recycled plastic blends were inferior to those made from virgin plastic blends, especially in elongation break. The morphological study verified that the interfacial adhesion or the compatibility of plastic blends with wood flour was improved by adding SEBS-g-MAH or in-situ grafting MAH. A better interfacial bonding between PP, HDPE, PS and wood flour was obtained by in-situ grafting MAH than the addition of SEBS-g-MAH. In-situ grafting MAH can be considered as a potential way of increasing the interfacial compatibility between plastic blends and wood flour. The storage modulus and damping factor of composites were also characterized through dynamic mechanical analysis （DMA）.展开更多
Wood-polymer composites (WPC) were prepared from wood fiber and four kinds of plastics such as PE, PS, ABS, and SAN. The effects of different modifiers on the mechanical properties of the composites were studied. The ...Wood-polymer composites (WPC) were prepared from wood fiber and four kinds of plastics such as PE, PS, ABS, and SAN. The effects of different modifiers on the mechanical properties of the composites were studied. The results showed modifiers could raise the bonding strength of wood fiber with polymer and improve the mechanical properties of the composites. Different modifiers had different effects on the properties of wood-polymer composites, and comparatively the modifier of isocyanate produced a better result. Wood-polymer composite takes not only the advantages of both wood fiber and polymer, but waterproof, dimensional stability and dynamic strength are also significantly improved. Key word Wood fiber - Thermoplastic polyester - Wood-polymer composites - Modifier - Mechanical properties CLC number TB332 Document code A Foundation item: This study was supported by the Harbin Technology Tackle Key Plan (Development Research of Wood-Polymer Composites with High Wood Matrix) and by Heilongjing Nature Science Fund (Composite Mechanism Study of the Wood Polymer).Biography: XU Min (1963-), Female, Associate professor in Material Science and Engineering College, Northeast Forestry University, Harbin 150040, P. R. China.Responsible editor: Chai Ruihai展开更多
Kevlar fiber （KF） is a synthesized product with strong mechanical properties. We used KF as a reinforcement to improve the mechanical properties of wood-flour/polypropylene （WF/PP） composites. KF was pretreated w...Kevlar fiber （KF） is a synthesized product with strong mechanical properties. We used KF as a reinforcement to improve the mechanical properties of wood-flour/polypropylene （WF/PP） composites. KF was pretreated with NaOH to improve its compatibility with the thermoplastic matrix. Maleated polypropylene （MAPP） was used as a coupling agent to improve the interfacial adhesion between KF, WF, and PP. Incorporation of KF improved the mechanical properties of WF/PP composites. Treatment of KF with NaOH resulted in further improvement in mechanical strength. Addition of 3% MAPP and 2% hydrolyzed KF （HKF） led to an increment of 93.8% in unnotched impact strength, 17.7% in notched impact strength, 86.8% in flexure strength, 50.8% in flexure modulus, and 94.1% in tensile strength compared to traditional WF/PP composites. Scanning electron microscopy of the cryo-fractured section of WF/PP showed that the HKF surface was rougher than the virgin KF, and the KF was randomly distributed in the composites, which might cause a mechanical interlocking between KF and polypropylene molecules in the composites.展开更多
Terpenes, aldehydes, ketones, benzene, and toluene are the important volatileorganic compounds (VOCs) emitted from wood composites. A sampling apparatus of VOCs for woodcomposites was designed and manufactured by Nort...Terpenes, aldehydes, ketones, benzene, and toluene are the important volatileorganic compounds (VOCs) emitted from wood composites. A sampling apparatus of VOCs for woodcomposites was designed and manufactured by Northeast Forestry University in China. Theconcentration of VOCs derived from wood based materials, such as flooring, panel wall, finishing,and furniture can be sampled in a small stainless steel chambers. A protocol is also developed inthis study to sample and measure the new and representative specimens. Preliminary research showedthat the properties of the equipment have good stability. The sort and the amount of differentcomponents can be detected from it. The apparatus is practicable.展开更多
We used paper mill sludge（PMS） to substitute for part of the wood fibers（WF） used to reinforce high density polyethylene（HDPE）.The resulting composites were subjected to xenon-arc weathering.The composite filled...We used paper mill sludge（PMS） to substitute for part of the wood fibers（WF） used to reinforce high density polyethylene（HDPE）.The resulting composites were subjected to xenon-arc weathering.The composite filled with limited PMS（under 10 %） had mechanical properties and aging resistance similar to those without PMS.The composites containing more PMS faded and cracked more readily than those without PMS.Based on the carbonyl index,crystallinity,and wood index,PMS appeared to accelerate the degradation of composites during weathering.Adding PMS to WF–HDPE composites reduced the weathering resistance,and this reduction was not significant if the PMS content did not exceed 20 % of the wood fibers.Therefore,PMS could be used as a reinforcement in wood-plastic composites at levels less than20 % of the wood fiber content.展开更多
Wood composites can generally be classified in three parts: laminated composites, mixed composites and penetrated composites. Every part has its own characteristic and can be further divided. This paper introduces the...Wood composites can generally be classified in three parts: laminated composites, mixed composites and penetrated composites. Every part has its own characteristic and can be further divided. This paper introduces the history and the state of development of wood composites in China. The research about glue-laminated timber is rare and the industry hardly comes to being. A great of achievements have been obtained in mixed composites and it is well industrialized. Many studies on scrimber have been done and the Chinese researchers are looking for a feasible way to develop the scrimber industry in China. Chinese researchers also spent so much energy in studying wood plastic composites (WPC), but it has not been industrialized due to the high cost.展开更多
Viscoelastic properties of maleated polypropylene （MAPP）-modified wood flour/polypropylene composites （WPC） were investigated by both a compression stress relaxation method and dynamic mechanical analyses （DMA）....Viscoelastic properties of maleated polypropylene （MAPP）-modified wood flour/polypropylene composites （WPC） were investigated by both a compression stress relaxation method and dynamic mechanical analyses （DMA）. Three wood to polymer ratios （40：60, 60：40, and 80：20） and five MAPP loading levels （0, 1, 2, 4 and 8%） were used to study their effects on the viscoelastic prop- erties of MAPP-WPC. The results show that： 1） higher wood to polymer ratio corresponds to higher stress relaxation levels for unmodified WPC. The modification with MAPP has an obvious effect on the stress relaxation of MAPP-WPC at higher wood to polymer ratios （60：40 and 80：20）, but almost no effect at the 40：60 wood to polymer ratio. The optimal MAPP loading level for the wood to polymer ratio of 60：40 appears at 1%; 2） the storage modulus reaches its maximum at a MAPP loading level of 1% for wood to polymer ratios of 40：60 and 60：40, while for the 80：20 wood to polymer ratio, a higher storage modulus is observed at higher MAPP loading levels, which is quite consistent with the stress relaxation results. The results suggested that a suitable loading level of MAPP has a positive effect on the viscoelastic properties of WPC at higher wood to polymer ratios. Excessive MAPP loading would have resulted in adverse effects.展开更多
We produced wood–plastic composite board by using sawmill wastage of mahogany（Swietenia macrophylla） wood and low density polyethylene.We used multi-response optimization to optimize the process parameters of compo...We produced wood–plastic composite board by using sawmill wastage of mahogany（Swietenia macrophylla） wood and low density polyethylene.We used multi-response optimization to optimize the process parameters of composite board production including mixing ratio,fire retardant（%） and pressing time（min）.We investigated the effects of these three process parameters in the mechanical and physical properties of the composite board.Afterwards,Box–Behnken design was performed as response surface methodology with desirability functions to attain the optimal level of mixing ratio,fire retardant and pressing time（min）.The maximum modulus of elasticity（MOE） and modulus of rupture（MOR） were achieved at the optimal conditions of wood plastic mixing ratio of60：40,pressing time of 9 min and zero fire retardant percentage.The optimized MOR and MOE were 13.12 and1,781.0 N mm-2,respectively.展开更多
Flax fiber(FF) was used to reinforce wood flour/high density polyethylene composites(WF/PE).WF/PE particles were uniformly mixed with FF via high-speed mixing and then extruded with a single screw extruder to prepare ...Flax fiber(FF) was used to reinforce wood flour/high density polyethylene composites(WF/PE).WF/PE particles were uniformly mixed with FF via high-speed mixing and then extruded with a single screw extruder to prepare FF reinforced WF/PE composites(FF/WF/PE).Mechanical testing,dynamic mechanical analysis,scanning electron microscopy(SEM),creep measurement and Torque rheology were used to characterize the resulting composites.The results indicate that the mechanical performance of the composites could be remarkably improved by adding a limited amount of FF.The flexural strength and modulus increased by 14.6 and 51.4%,respectively(FF content of 9 wt%),while the unnotched impact strength could be increased by 26.5%(FF content of12 wt%).The creep resistance and toughness of thecomposite was markedly improved without changing the plastic content of the composite material.展开更多
As a hot-melt adhesive, ethylene-vinyl-acetate （EVA） has been used in many industrial applications. But studies of the application of EVA in wood-plastic composites （WPC） are relatively few, so we have investigate...As a hot-melt adhesive, ethylene-vinyl-acetate （EVA） has been used in many industrial applications. But studies of the application of EVA in wood-plastic composites （WPC） are relatively few, so we have investigated the proposition of whether EVA is a suitable coupling agent for WPC or not. The results show that EVA with 8% VA is not a suitable coupling agent, because it reduces the mechanical properties of WPC without any significant effect on its physical properties. With an increase in the amount of wood powder, the mechanical properties of WPC decrease and the ability of water absorption of WPC increases.展开更多
X-ray is irradiated in some wood composites(multi-layer particleboard.sin-gle-layer particleboard,reconsolidated wood,).According to the gray degree principle(0-255 grade degree)and the corresponding relation between ...X-ray is irradiated in some wood composites(multi-layer particleboard.sin-gle-layer particleboard,reconsolidated wood,).According to the gray degree principle(0-255 grade degree)and the corresponding relation between density and gray,X-raynegatives are scanned.The numbers and pictures of every degree density are obtained andaccurate composite densities are counted.展开更多
The mechanical properties of composites prepared from wood flour and thermoplastic blends were investigated. Thermoplastic mixtures of polypropylene (PP) and high-density polyethylene (HDPE) and polystyrene (PS), virg...The mechanical properties of composites prepared from wood flour and thermoplastic blends were investigated. Thermoplastic mixtures of polypropylene (PP) and high-density polyethylene (HDPE) and polystyrene (PS), virgin or recycled, were mixed with wood flour in a high speed blender and then extruded by a specially designed twin/single screw extruder system to form wood-flour/thermoplastic-blends composites (WTBCs). Comparative studies were made to evaluate the effectiveness of the two modification methods of the thermoplastic blends, the one of the addition of maleic anhydride grafted styrene-ethylene-butylene-styrene block copolymer (SEBS-g-MAH) as compatibilizer and the other of blend grafting of maleic anhydride (MAH) using dicumyl peroxide (DCP) as initiator by reactive extrusion. The results showed that the impact properties of WTBCs using SEBS-g-MAH as compatilizer were better improved than that of the blend grafting. However, adverse results were observed on the tensile and flexural properties of the corresponding WTBCs. The mechanical properties of WTBCs prepared from recycled plastic blends were poorer to some extent than that from virgin plastic blends in general, especially in elongation break. The morphology of WTBCs breaking section was analyzed by scanning electron microscopy (SEM) and the results showed that a good interfacial adhesion between wood flour and polymer matrix was observed with both of the two modification methods. However, by blend grafting of adding DCP as initiator and MAH as monomer, a better interfacial bonding between wood and plastic matrix was obtained than that of the addition of SEBS-g-MAH. Blend grafting can be considered as a potential way of increasing the interfacial compatibility of different plastics and between plastic blends and wood.展开更多
A study was conducted to investigate the effects of compatibilizers, including Maleic anhydride grafted polypropylene （MA-PP） and maleic anhydride grafted ethylene-propylene-diene copolymer （MA-EPDM）, on wood-flou...A study was conducted to investigate the effects of compatibilizers, including Maleic anhydride grafted polypropylene （MA-PP） and maleic anhydride grafted ethylene-propylene-diene copolymer （MA-EPDM）, on wood-flour/polypropylene （WF/PP） composites. WF/PP composites were prepared by direct extrusion profiles using a twin-screw/single-screw extruder system. DMA analysis showed that the loss factor of composites decreased and the storage modulus improved in the presence of MA-PP, which indicated much better interfacial adhesion between the PP matrix and wood flour filler than in the absence of compatibilizer. Morphological feature based on SEM observation showed that MA-PP and MA-EPDM improved the dispersion of the wood particles in the plastic matrix. MA-EPDM is a soft segment, although it improved the interfacial adhesion, storage modulus decreases with adding of MA-EPDM. As compatibilizer of wood-flour/polypropylene composites, both DMA analysis and SEM feature proved that MA-PP was superior to MA-EPDM.展开更多
MA-SEBS as compatibilizer and impact modifier was incorporated into Polypropylene/Wood Fiber （PP/WF） to enhance interface adhesion and impact strength of the composite. The effect of MA-SEBS content on the impact fr...MA-SEBS as compatibilizer and impact modifier was incorporated into Polypropylene/Wood Fiber （PP/WF） to enhance interface adhesion and impact strength of the composite. The effect of MA-SEBS content on the impact fracture behavior of PP/WF composites was studied. The impact properties of composites with 8% MA-SEBS reached the maximum value. And further increasing of MA-SEBS content to 10% did not improve the fracture toughness, but improved the stiffness of composites by DMA analysis. This was attributed to the improved PP/WF adhesion. As the MA-SEBS content is more than 8%, the molecule interaction of PP and WF was expected to much stronger than lower MA-SEBS. Scanning electron microscopy （SEM） was performed to analyze the impact fracture surface and showed a stronger affinity for the wood surfaces.展开更多
The chemical composition of unpleasant smell, emitted from the production process of wood-plastic composites using Manchurian ash sawdust （Fraxinus mandschurica Rupr.） and polypropylene powder as the raw material, w...The chemical composition of unpleasant smell, emitted from the production process of wood-plastic composites using Manchurian ash sawdust （Fraxinus mandschurica Rupr.） and polypropylene powder as the raw material, was investigated. Wood sawdust and polypropylene powder were subjected to heat treatment to 290℃ during 8 min （the conditions were similar to those employed on an industrial scale）. The emitted compounds were collected and analyzed by gas chromatography-mass spectrometry （GC-MS）. The analytical results showed that the unpleasant smell was emitted from the pyrogenation of wood sawdust rather than from the polypropylene powder. Nine types of compounds （hydrocarbons, ethers, phenols, aldehydes, ketones, alcohols, acids and their derivatives, furan and its derivatives, and nitrogen-containing compounds） were collected in the gas phase during heating. Among those 126 components detected by GC-MS, 112 compounds were identified.展开更多
Electrical and electromagnetic shielding wood metal composite was prepared by using electroless nickel plating. The effects of solution amount, plating time and plating temperature on surface resistivity and electroma...Electrical and electromagnetic shielding wood metal composite was prepared by using electroless nickel plating. The effects of solution amount, plating time and plating temperature on surface resistivity and electromagnetic shielding effectiveness were investigated. And P content, microstructure and surface feature of layers obtained at different temperatures were analyzed by energy dispersion spectrometer （EDS）, X-ray diffraction （XRI）） and scanning electron microscopy （SEM）. The results showed that layers with higher electro-conductivity and electromagnetic shielding effectiveness were obtained under the optimum conditions that plating solution was 500 mL, plating time was 30 min and plating temperature was 62℃. The results showed by EDS analysis; that P content increased gradually in a small extent with plating temperature increased. It was showed by XRD and SEM analysis that layers plated at different temperatures were all microcrystalline structure and uniform and successive, which had noticeable metal luster. Those indicated that plating temperature had little influence on microstructure and surface feature under pH value invariable.展开更多
To clarify liquefaction ratios and their construction variations of the main chemical compositions of wood in phenol using phosphoric acid as a catalyst, the chemical ingredients of wood such as holocellulose, cellulo...To clarify liquefaction ratios and their construction variations of the main chemical compositions of wood in phenol using phosphoric acid as a catalyst, the chemical ingredients of wood such as holocellulose, cellulose and lignin, were measured and extracted according to GB methods. With Fourier transform infrared （FTIR）, the product identification of reactant before and after liquefaction in phenol was investigated. The molecular weights and their distributions of the liquefaction results （acetone soluble parts） were studied by gel permeation chromatography （GPC）. Results show that the molecular weights and their distributions of poplar and Chinese fir are almost the same. In poplar, the distribution of cellulose is the largest, and that ofholocellulose the smallest after liquefaction. For Chinese fir, the distribution of holocellulose is the largest, and that of cellulose the smallest. After liquefaction of poplar cellulose, the change bands of FTIR spectrum observed below 1 600 cm^-1, can be attributed to new substitute groups. The same is true for poplar lignin. For Chinese fir, the spectra of liquefaction results of all chemical compositions differ from that of wood meal. This reveals the more activity groups were produced because of the reactions between Chinese fir and phenol. The research shows that the liquefaction ratios of poplar decrease in the following order： holocellulose 〉 lignin 〉 cellulose, and those of Chinese fir in the order： lignin 〉 cellulose 〉 holocellulose.展开更多
For this study, an intercalation compounding method was used to prepare Chinese fir wood/Ca-montmorillonite （Ca-MMT） composite board to improve its properties such as surface mechanical properties, flame retardance ...For this study, an intercalation compounding method was used to prepare Chinese fir wood/Ca-montmorillonite （Ca-MMT） composite board to improve its properties such as surface mechanical properties, flame retardance and dimensional stability. By virtue of water-soluble phenolic resin （PF）, Chinese fir wood and Ca-MMT were mixed by pressure and vacuum impregnation. The optimum impregnation technology of Chinese fir wood/Ca-MMT composite board was obtained by using an orthogonal design and a single factor design of pressure and vacuum impregnation, using weight percent gain （WPG） as the basic index. The results are as follows： 1） On the basis of the orthogonal design and an actual experiment, the optimum preparation technology of Chinese fir wood/Ca-MMT composite board is 20% PF resin dispersion concentration （wt%）, 1.0 CEC amount of organic intercalation agent, 0.098 MPa vacuum degree, 5% concentration of Ca-MMT and 1.0 MPa pressure. 2） The WPG of the composite board samples of 450 mm length was much larger than that of the samples of 600, 750 and 900 mm length. Warm water extraction contributed little to WPG展开更多
Wood plastic composite （WPC） of wood flour （WF）, high density polyethylene （HDPE）, maleic anhydride-grafted polyethylene （MAPE） and lubricant was prepared by extrusion, and then exposed to different temperatur...Wood plastic composite （WPC） of wood flour （WF）, high density polyethylene （HDPE）, maleic anhydride-grafted polyethylene （MAPE） and lubricant was prepared by extrusion, and then exposed to different temperatures to evaluate the effects of freezing and thermal treatment on its dimensional and mechanical properties. At elevated temperatures, WPC expanded rapidly initially, and then contracted slowly until reaching an equilibrium state. Treatment at 52°C and relative humidity of 50% for 16 days improved the mechanical properties of WPC： flexure, tensile strength, and izod unnotched impact strength increased by 8%, 10% and 15%, respectively. Wide-angle X-ray diffraction （XRD） tests showed that the degree of crystalization of HDPE in WPC declined with increasing treatment temperature.展开更多
文摘For evaluation of the rheological and mechanical properties of highly filled wood plastic composites （WPCs）, polypropylene/polyethylene （PP/PE） blends were grafted with maleic anhydride （MAH） to enhance the interfacial adhesion between wood fiber and matrix. WPCs were prepared from wood fiber up to 60 wt.% and modified PP/PE was blended by extrusion. The rheological properties were studied by using dynamic measurement. According to the strain sweep test, the linear viscoelastic region of composites in the melt was determined. The result showed that the storage modulus was independent of the strain at low strain region （〈0.1%）. The frequency sweep resuits indicated that all composites exhibited shear thinning behavior, and both the storage modulus and complex viscosity of MAH modified composites were decreased comparing to those unmodified. Flexural properties and impact strength of the prepared WPCs were measured according to the relevant standard specifications. The flexural and impact strength of the manufactured composites significantly increased and reached a maximum when MAH dosage was 1.0 wt%, whereas the flexural modulus after an initial decreased, also increased with MAH dosage. The increase in mechanical properties indicated that the presence of anhydride groups enhanced the interracial adhesion between wood fiber and PP/PE blends.
基金supported by the National High Technology Research and Development Program of China(2010AA101703)the Natural Science Foundation of Heilongjiang Province of China (C200950)the Fundamental Research Fundsfor the Central Universities (DL09BB38)
文摘The effect of maleic anhydride grafted styrene-ethylene- buty-lene-styrene block copolymer （SEBS-g-MAH） and in-situ grafting MAH on mechanical, dynamic mechanical properties of wood flour/recycled plastic blends composites was investigated. Recycled plastic polypro-pylene （PP）, high-density polyethylene （HDPE） and polystyrene （PS）, were mixed with wood flour in a high speed blender and then extruded by a twin/single screw tandem extruder system to form wood flour/recycled plastic blends composites. Results show that the impact properties of the composites were improved more significantly by using SEBS-g-MAH compatibilizer than by using the mixtures of MAH and DCP via reactive blending in situ. However, contrary results were ob-served on the tensile and flexural properties of the corresponding com-posites. In General, the mechanical properties of composites made from recycled plastic blends were inferior to those made from virgin plastic blends, especially in elongation break. The morphological study verified that the interfacial adhesion or the compatibility of plastic blends with wood flour was improved by adding SEBS-g-MAH or in-situ grafting MAH. A better interfacial bonding between PP, HDPE, PS and wood flour was obtained by in-situ grafting MAH than the addition of SEBS-g-MAH. In-situ grafting MAH can be considered as a potential way of increasing the interfacial compatibility between plastic blends and wood flour. The storage modulus and damping factor of composites were also characterized through dynamic mechanical analysis （DMA）.
基金Supported by the Harbin Technology Tackle Key Plan (Development Research of Wood-Polymer Composites with High Wood Matrix) and by Heilongjing Nature Science Fund (Composite Mechanism Study of the Wood Polymer).
文摘Wood-polymer composites (WPC) were prepared from wood fiber and four kinds of plastics such as PE, PS, ABS, and SAN. The effects of different modifiers on the mechanical properties of the composites were studied. The results showed modifiers could raise the bonding strength of wood fiber with polymer and improve the mechanical properties of the composites. Different modifiers had different effects on the properties of wood-polymer composites, and comparatively the modifier of isocyanate produced a better result. Wood-polymer composite takes not only the advantages of both wood fiber and polymer, but waterproof, dimensional stability and dynamic strength are also significantly improved. Key word Wood fiber - Thermoplastic polyester - Wood-polymer composites - Modifier - Mechanical properties CLC number TB332 Document code A Foundation item: This study was supported by the Harbin Technology Tackle Key Plan (Development Research of Wood-Polymer Composites with High Wood Matrix) and by Heilongjing Nature Science Fund (Composite Mechanism Study of the Wood Polymer).Biography: XU Min (1963-), Female, Associate professor in Material Science and Engineering College, Northeast Forestry University, Harbin 150040, P. R. China.Responsible editor: Chai Ruihai
基金supported by the National Natural Science Foundation of China (Project Nos. 31010103905 and31070507)Program for New Century Excellent Talents in University of Ministry of Education of China (NCET-11-0608)the Fundamental Research Funds for the Central Universities (DL12DB02)
文摘Kevlar fiber （KF） is a synthesized product with strong mechanical properties. We used KF as a reinforcement to improve the mechanical properties of wood-flour/polypropylene （WF/PP） composites. KF was pretreated with NaOH to improve its compatibility with the thermoplastic matrix. Maleated polypropylene （MAPP） was used as a coupling agent to improve the interfacial adhesion between KF, WF, and PP. Incorporation of KF improved the mechanical properties of WF/PP composites. Treatment of KF with NaOH resulted in further improvement in mechanical strength. Addition of 3% MAPP and 2% hydrolyzed KF （HKF） led to an increment of 93.8% in unnotched impact strength, 17.7% in notched impact strength, 86.8% in flexure strength, 50.8% in flexure modulus, and 94.1% in tensile strength compared to traditional WF/PP composites. Scanning electron microscopy of the cryo-fractured section of WF/PP showed that the HKF surface was rougher than the virgin KF, and the KF was randomly distributed in the composites, which might cause a mechanical interlocking between KF and polypropylene molecules in the composites.
基金This project is supported by the grand of the Oversea Back Scholar Research Startup of China Education Ministry, Heilongjiang Post-doctorial Research Startup and NEFU Creative Item.
文摘Terpenes, aldehydes, ketones, benzene, and toluene are the important volatileorganic compounds (VOCs) emitted from wood composites. A sampling apparatus of VOCs for woodcomposites was designed and manufactured by Northeast Forestry University in China. Theconcentration of VOCs derived from wood based materials, such as flooring, panel wall, finishing,and furniture can be sampled in a small stainless steel chambers. A protocol is also developed inthis study to sample and measure the new and representative specimens. Preliminary research showedthat the properties of the equipment have good stability. The sort and the amount of differentcomponents can be detected from it. The apparatus is practicable.
基金supported by the "Special Fund for Forestry Research in the Public Interest(201204802-1)"the "Nature Science Foundation of China(31070506)"
文摘We used paper mill sludge（PMS） to substitute for part of the wood fibers（WF） used to reinforce high density polyethylene（HDPE）.The resulting composites were subjected to xenon-arc weathering.The composite filled with limited PMS（under 10 %） had mechanical properties and aging resistance similar to those without PMS.The composites containing more PMS faded and cracked more readily than those without PMS.Based on the carbonyl index,crystallinity,and wood index,PMS appeared to accelerate the degradation of composites during weathering.Adding PMS to WF–HDPE composites reduced the weathering resistance,and this reduction was not significant if the PMS content did not exceed 20 % of the wood fibers.Therefore,PMS could be used as a reinforcement in wood-plastic composites at levels less than20 % of the wood fiber content.
文摘Wood composites can generally be classified in three parts: laminated composites, mixed composites and penetrated composites. Every part has its own characteristic and can be further divided. This paper introduces the history and the state of development of wood composites in China. The research about glue-laminated timber is rare and the industry hardly comes to being. A great of achievements have been obtained in mixed composites and it is well industrialized. Many studies on scrimber have been done and the Chinese researchers are looking for a feasible way to develop the scrimber industry in China. Chinese researchers also spent so much energy in studying wood plastic composites (WPC), but it has not been industrialized due to the high cost.
基金supported by the National Natural Science Foundation of China (Grant No. 30871966)
文摘Viscoelastic properties of maleated polypropylene （MAPP）-modified wood flour/polypropylene composites （WPC） were investigated by both a compression stress relaxation method and dynamic mechanical analyses （DMA）. Three wood to polymer ratios （40：60, 60：40, and 80：20） and five MAPP loading levels （0, 1, 2, 4 and 8%） were used to study their effects on the viscoelastic prop- erties of MAPP-WPC. The results show that： 1） higher wood to polymer ratio corresponds to higher stress relaxation levels for unmodified WPC. The modification with MAPP has an obvious effect on the stress relaxation of MAPP-WPC at higher wood to polymer ratios （60：40 and 80：20）, but almost no effect at the 40：60 wood to polymer ratio. The optimal MAPP loading level for the wood to polymer ratio of 60：40 appears at 1%; 2） the storage modulus reaches its maximum at a MAPP loading level of 1% for wood to polymer ratios of 40：60 and 60：40, while for the 80：20 wood to polymer ratio, a higher storage modulus is observed at higher MAPP loading levels, which is quite consistent with the stress relaxation results. The results suggested that a suitable loading level of MAPP has a positive effect on the viscoelastic properties of WPC at higher wood to polymer ratios. Excessive MAPP loading would have resulted in adverse effects.
文摘We produced wood–plastic composite board by using sawmill wastage of mahogany（Swietenia macrophylla） wood and low density polyethylene.We used multi-response optimization to optimize the process parameters of composite board production including mixing ratio,fire retardant（%） and pressing time（min）.We investigated the effects of these three process parameters in the mechanical and physical properties of the composite board.Afterwards,Box–Behnken design was performed as response surface methodology with desirability functions to attain the optimal level of mixing ratio,fire retardant and pressing time（min）.The maximum modulus of elasticity（MOE） and modulus of rupture（MOR） were achieved at the optimal conditions of wood plastic mixing ratio of60：40,pressing time of 9 min and zero fire retardant percentage.The optimized MOR and MOE were 13.12 and1,781.0 N mm-2,respectively.
基金supported by the Natural Science Foundation of China(Grant No.31600459)the Natural Science Foundation of Heilongjiang Province of China(Grant No.C2016001)
文摘Flax fiber(FF) was used to reinforce wood flour/high density polyethylene composites(WF/PE).WF/PE particles were uniformly mixed with FF via high-speed mixing and then extruded with a single screw extruder to prepare FF reinforced WF/PE composites(FF/WF/PE).Mechanical testing,dynamic mechanical analysis,scanning electron microscopy(SEM),creep measurement and Torque rheology were used to characterize the resulting composites.The results indicate that the mechanical performance of the composites could be remarkably improved by adding a limited amount of FF.The flexural strength and modulus increased by 14.6 and 51.4%,respectively(FF content of 9 wt%),while the unnotched impact strength could be increased by 26.5%(FF content of12 wt%).The creep resistance and toughness of thecomposite was markedly improved without changing the plastic content of the composite material.
文摘As a hot-melt adhesive, ethylene-vinyl-acetate （EVA） has been used in many industrial applications. But studies of the application of EVA in wood-plastic composites （WPC） are relatively few, so we have investigated the proposition of whether EVA is a suitable coupling agent for WPC or not. The results show that EVA with 8% VA is not a suitable coupling agent, because it reduces the mechanical properties of WPC without any significant effect on its physical properties. With an increase in the amount of wood powder, the mechanical properties of WPC decrease and the ability of water absorption of WPC increases.
文摘X-ray is irradiated in some wood composites(multi-layer particleboard.sin-gle-layer particleboard,reconsolidated wood,).According to the gray degree principle(0-255 grade degree)and the corresponding relation between density and gray,X-raynegatives are scanned.The numbers and pictures of every degree density are obtained andaccurate composite densities are counted.
文摘The mechanical properties of composites prepared from wood flour and thermoplastic blends were investigated. Thermoplastic mixtures of polypropylene (PP) and high-density polyethylene (HDPE) and polystyrene (PS), virgin or recycled, were mixed with wood flour in a high speed blender and then extruded by a specially designed twin/single screw extruder system to form wood-flour/thermoplastic-blends composites (WTBCs). Comparative studies were made to evaluate the effectiveness of the two modification methods of the thermoplastic blends, the one of the addition of maleic anhydride grafted styrene-ethylene-butylene-styrene block copolymer (SEBS-g-MAH) as compatibilizer and the other of blend grafting of maleic anhydride (MAH) using dicumyl peroxide (DCP) as initiator by reactive extrusion. The results showed that the impact properties of WTBCs using SEBS-g-MAH as compatilizer were better improved than that of the blend grafting. However, adverse results were observed on the tensile and flexural properties of the corresponding WTBCs. The mechanical properties of WTBCs prepared from recycled plastic blends were poorer to some extent than that from virgin plastic blends in general, especially in elongation break. The morphology of WTBCs breaking section was analyzed by scanning electron microscopy (SEM) and the results showed that a good interfacial adhesion between wood flour and polymer matrix was observed with both of the two modification methods. However, by blend grafting of adding DCP as initiator and MAH as monomer, a better interfacial bonding between wood and plastic matrix was obtained than that of the addition of SEBS-g-MAH. Blend grafting can be considered as a potential way of increasing the interfacial compatibility of different plastics and between plastic blends and wood.
基金This paper was supported by National Foundation of Application of Agricultural Scientific and Technological Achievements (2006GB23600450).
文摘A study was conducted to investigate the effects of compatibilizers, including Maleic anhydride grafted polypropylene （MA-PP） and maleic anhydride grafted ethylene-propylene-diene copolymer （MA-EPDM）, on wood-flour/polypropylene （WF/PP） composites. WF/PP composites were prepared by direct extrusion profiles using a twin-screw/single-screw extruder system. DMA analysis showed that the loss factor of composites decreased and the storage modulus improved in the presence of MA-PP, which indicated much better interfacial adhesion between the PP matrix and wood flour filler than in the absence of compatibilizer. Morphological feature based on SEM observation showed that MA-PP and MA-EPDM improved the dispersion of the wood particles in the plastic matrix. MA-EPDM is a soft segment, although it improved the interfacial adhesion, storage modulus decreases with adding of MA-EPDM. As compatibilizer of wood-flour/polypropylene composites, both DMA analysis and SEM feature proved that MA-PP was superior to MA-EPDM.
基金This paper was supported by National 863 Program (2002AA245141)national Foundation of Application of Agricul-tural Scientific and Technological Achievements (2006GB23600450)
文摘MA-SEBS as compatibilizer and impact modifier was incorporated into Polypropylene/Wood Fiber （PP/WF） to enhance interface adhesion and impact strength of the composite. The effect of MA-SEBS content on the impact fracture behavior of PP/WF composites was studied. The impact properties of composites with 8% MA-SEBS reached the maximum value. And further increasing of MA-SEBS content to 10% did not improve the fracture toughness, but improved the stiffness of composites by DMA analysis. This was attributed to the improved PP/WF adhesion. As the MA-SEBS content is more than 8%, the molecule interaction of PP and WF was expected to much stronger than lower MA-SEBS. Scanning electron microscopy （SEM） was performed to analyze the impact fracture surface and showed a stronger affinity for the wood surfaces.
文摘The chemical composition of unpleasant smell, emitted from the production process of wood-plastic composites using Manchurian ash sawdust （Fraxinus mandschurica Rupr.） and polypropylene powder as the raw material, was investigated. Wood sawdust and polypropylene powder were subjected to heat treatment to 290℃ during 8 min （the conditions were similar to those employed on an industrial scale）. The emitted compounds were collected and analyzed by gas chromatography-mass spectrometry （GC-MS）. The analytical results showed that the unpleasant smell was emitted from the pyrogenation of wood sawdust rather than from the polypropylene powder. Nine types of compounds （hydrocarbons, ethers, phenols, aldehydes, ketones, alcohols, acids and their derivatives, furan and its derivatives, and nitrogen-containing compounds） were collected in the gas phase during heating. Among those 126 components detected by GC-MS, 112 compounds were identified.
基金The research was supported by the National Natural Science Foundation of China （30571454）. Natural Science Foundation of Heilongjiang Province （C0210） and Harbin City Youth Science Faud （2004AFQXJ027）.
文摘Electrical and electromagnetic shielding wood metal composite was prepared by using electroless nickel plating. The effects of solution amount, plating time and plating temperature on surface resistivity and electromagnetic shielding effectiveness were investigated. And P content, microstructure and surface feature of layers obtained at different temperatures were analyzed by energy dispersion spectrometer （EDS）, X-ray diffraction （XRI）） and scanning electron microscopy （SEM）. The results showed that layers with higher electro-conductivity and electromagnetic shielding effectiveness were obtained under the optimum conditions that plating solution was 500 mL, plating time was 30 min and plating temperature was 62℃. The results showed by EDS analysis; that P content increased gradually in a small extent with plating temperature increased. It was showed by XRD and SEM analysis that layers plated at different temperatures were all microcrystalline structure and uniform and successive, which had noticeable metal luster. Those indicated that plating temperature had little influence on microstructure and surface feature under pH value invariable.
基金Supported by the Key Research Program Foundation, Ministry of Educational of China (Grant No.02021)the National Natural Science Foundation of China (Grant No. 30471351)
文摘To clarify liquefaction ratios and their construction variations of the main chemical compositions of wood in phenol using phosphoric acid as a catalyst, the chemical ingredients of wood such as holocellulose, cellulose and lignin, were measured and extracted according to GB methods. With Fourier transform infrared （FTIR）, the product identification of reactant before and after liquefaction in phenol was investigated. The molecular weights and their distributions of the liquefaction results （acetone soluble parts） were studied by gel permeation chromatography （GPC）. Results show that the molecular weights and their distributions of poplar and Chinese fir are almost the same. In poplar, the distribution of cellulose is the largest, and that ofholocellulose the smallest after liquefaction. For Chinese fir, the distribution of holocellulose is the largest, and that of cellulose the smallest. After liquefaction of poplar cellulose, the change bands of FTIR spectrum observed below 1 600 cm^-1, can be attributed to new substitute groups. The same is true for poplar lignin. For Chinese fir, the spectra of liquefaction results of all chemical compositions differ from that of wood meal. This reveals the more activity groups were produced because of the reactions between Chinese fir and phenol. The research shows that the liquefaction ratios of poplar decrease in the following order： holocellulose 〉 lignin 〉 cellulose, and those of Chinese fir in the order： lignin 〉 cellulose 〉 holocellulose.
基金the National Natural Science Foundation of China (Grant No.30271055)
文摘For this study, an intercalation compounding method was used to prepare Chinese fir wood/Ca-montmorillonite （Ca-MMT） composite board to improve its properties such as surface mechanical properties, flame retardance and dimensional stability. By virtue of water-soluble phenolic resin （PF）, Chinese fir wood and Ca-MMT were mixed by pressure and vacuum impregnation. The optimum impregnation technology of Chinese fir wood/Ca-MMT composite board was obtained by using an orthogonal design and a single factor design of pressure and vacuum impregnation, using weight percent gain （WPG） as the basic index. The results are as follows： 1） On the basis of the orthogonal design and an actual experiment, the optimum preparation technology of Chinese fir wood/Ca-MMT composite board is 20% PF resin dispersion concentration （wt%）, 1.0 CEC amount of organic intercalation agent, 0.098 MPa vacuum degree, 5% concentration of Ca-MMT and 1.0 MPa pressure. 2） The WPG of the composite board samples of 450 mm length was much larger than that of the samples of 600, 750 and 900 mm length. Warm water extraction contributed little to WPG
基金support by the Chinese Science and Technology Support Program (Project No. 2012BAD32B04)the Fundamental Research Funds for the Central Universities(DL11BB37)
文摘Wood plastic composite （WPC） of wood flour （WF）, high density polyethylene （HDPE）, maleic anhydride-grafted polyethylene （MAPE） and lubricant was prepared by extrusion, and then exposed to different temperatures to evaluate the effects of freezing and thermal treatment on its dimensional and mechanical properties. At elevated temperatures, WPC expanded rapidly initially, and then contracted slowly until reaching an equilibrium state. Treatment at 52°C and relative humidity of 50% for 16 days improved the mechanical properties of WPC： flexure, tensile strength, and izod unnotched impact strength increased by 8%, 10% and 15%, respectively. Wide-angle X-ray diffraction （XRD） tests showed that the degree of crystalization of HDPE in WPC declined with increasing treatment temperature.