Aseries of [(Fe_(0.6)Co_(0.2)Ni_(0.2))_(0.75-0.03x)B_(0.2)Si_(0.05+0.03x)]_(96)Nb_(4) amorphous alloy composite coatings were prepared by adjusting the silicon content(x=0,1,2,3,4,5,and 6)and their microstructures and...Aseries of [(Fe_(0.6)Co_(0.2)Ni_(0.2))_(0.75-0.03x)B_(0.2)Si_(0.05+0.03x)]_(96)Nb_(4) amorphous alloy composite coatings were prepared by adjusting the silicon content(x=0,1,2,3,4,5,and 6)and their microstructures and tribological properties were investigated by laser cladding technique.Additionally,the effect of Si on the glass forming ability(GFA)of the layers was understood.Results show that an appropriate Si content can refine the microstructure of the FeCoNiBSiNb laser cladding layers and improve the mechanical and tribological properties.The hardness of the coating layer increases monotonically with the Si content.At the Si content of 4.8at%(x=0),the coating layer exhibits a relatively low hardness(734.2HV 0.1).Conversely,at the silicon content of 13.44at%(x=3),the coating layer exhibits the highest hardness(1106HV 0.1).The non-crystalline content and tensile strength exhibit an initial increase,followed by a subsequent decrease.At x=2,the coating exhibits its maximum fracture strength(2880 MPa).However,when x>2,the fracture strength of the coating decreases with an increase in x.Conversely,with an increase in Si content,the wear volume loss initially decreases and then increases.At a Si content of 10.56at%(x=2),the coating exhibits the highest non-crystalline content(42%),the highest tensile strength(2880 MPa),and the most favorable dry friction performance.展开更多
This work is aimed to study the effect of boron on wear resistance of Fe-Cr-B alloys containing different boron contents(0 wt%,5 wt%,7 wt%and 9 wt%)from room temperature(RT)to 800°C in order to explore their appl...This work is aimed to study the effect of boron on wear resistance of Fe-Cr-B alloys containing different boron contents(0 wt%,5 wt%,7 wt%and 9 wt%)from room temperature(RT)to 800°C in order to explore their applications as high-temperature wear resistant mechanical parts.Additionally,the wear mechanism of alloys is evaluated.The tribological properties of alloys are systematically studied by using a ball-on-disc tribometer at 10 N and 0.20 m/s from RT to 800°C sliding against Si3N4 ceramic ball.The boron element greatly improves the wear resistance of specimens as compared with that of unreinforced specimen.The friction coefficients of specimens decrease with increasing of testing temperature.The wear rates of Fe-Cr-B alloys decrease firstly and then raise with the increase of boron content.The specific wear rates of specimens with boron are 1/10 of the unreinforced specimen.Fe-21wt%Cr-7wt%B keeps the best tribological properties at high temperature.展开更多
Despite the great achievements made in improvement of wear resistance properties of aluminum alloys, their applications in heavy surface load-bearing are limited. Single coating is insufficient to produce the desired ...Despite the great achievements made in improvement of wear resistance properties of aluminum alloys, their applications in heavy surface load-bearing are limited. Single coating is insufficient to produce the desired combination of surface properties. These problems can be solved through the duplex coatings. The aim of the present study is to overview the research advances on processes of duplex coatings on (aluminum) alloys combined with micro plasma oxidation process and with other modern processes such as physical vapour deposition and plasma assisted chemical vapour deposition and also to evaluate the performance of micro plasma oxidation coatings in improving the load-bearing, friction and wear resistance properties of aluminum alloys in comparison with other coatings. Wherein, a more detailed presentation of the processes and their performances and disadvantages are given as well.展开更多
Anodic films were successfully fabricated on Ti6A14V alloy by anodic oxidation method in an environmental friendly electrolyte with and without sodium hypochlorite. The anodic films were characterized by means of the ...Anodic films were successfully fabricated on Ti6A14V alloy by anodic oxidation method in an environmental friendly electrolyte with and without sodium hypochlorite. The anodic films were characterized by means of the scanning electron microscope （SEM） and energy dispersive spectrometer （EDS）. Results revealed that the addition of sodium hypochlorite leads to the ultrafast growth of oxide films, and results in the significant changes of morphology and thickness. The influence of sodium hypochlorite on formation and crystallization of oxide films as a function of anodizing time was discussed. Meanwhile, potentiodynamic electrochemical tests and dry sliding wear tests were performed to evaluate the corrosion resistance and tribological properties of oxide films. It was found that the oxide film fabricated with the existence of sodium hypochlorite had improved corrosion resistance and tribological properties than the one formed without sodium hypochlorite. Moreover, the effect mechanism of sodium hypochlorite on the growth rate and surface morphologies of oxide films during the anodizing process was discussed. It was found that hypochlorite ions participated in the reaction on anode which causes the rapid growth of oxide films and then affect the whole anodizing process.展开更多
文摘Aseries of [(Fe_(0.6)Co_(0.2)Ni_(0.2))_(0.75-0.03x)B_(0.2)Si_(0.05+0.03x)]_(96)Nb_(4) amorphous alloy composite coatings were prepared by adjusting the silicon content(x=0,1,2,3,4,5,and 6)and their microstructures and tribological properties were investigated by laser cladding technique.Additionally,the effect of Si on the glass forming ability(GFA)of the layers was understood.Results show that an appropriate Si content can refine the microstructure of the FeCoNiBSiNb laser cladding layers and improve the mechanical and tribological properties.The hardness of the coating layer increases monotonically with the Si content.At the Si content of 4.8at%(x=0),the coating layer exhibits a relatively low hardness(734.2HV 0.1).Conversely,at the silicon content of 13.44at%(x=3),the coating layer exhibits the highest hardness(1106HV 0.1).The non-crystalline content and tensile strength exhibit an initial increase,followed by a subsequent decrease.At x=2,the coating exhibits its maximum fracture strength(2880 MPa).However,when x>2,the fracture strength of the coating decreases with an increase in x.Conversely,with an increase in Si content,the wear volume loss initially decreases and then increases.At a Si content of 10.56at%(x=2),the coating exhibits the highest non-crystalline content(42%),the highest tensile strength(2880 MPa),and the most favorable dry friction performance.
基金Projects(51775365,51405329) supported by the National Natural Science Foundation of ChinaProject(2015M570239) supported by the China Postdoctoral Science Foundation
文摘This work is aimed to study the effect of boron on wear resistance of Fe-Cr-B alloys containing different boron contents(0 wt%,5 wt%,7 wt%and 9 wt%)from room temperature(RT)to 800°C in order to explore their applications as high-temperature wear resistant mechanical parts.Additionally,the wear mechanism of alloys is evaluated.The tribological properties of alloys are systematically studied by using a ball-on-disc tribometer at 10 N and 0.20 m/s from RT to 800°C sliding against Si3N4 ceramic ball.The boron element greatly improves the wear resistance of specimens as compared with that of unreinforced specimen.The friction coefficients of specimens decrease with increasing of testing temperature.The wear rates of Fe-Cr-B alloys decrease firstly and then raise with the increase of boron content.The specific wear rates of specimens with boron are 1/10 of the unreinforced specimen.Fe-21wt%Cr-7wt%B keeps the best tribological properties at high temperature.
文摘Despite the great achievements made in improvement of wear resistance properties of aluminum alloys, their applications in heavy surface load-bearing are limited. Single coating is insufficient to produce the desired combination of surface properties. These problems can be solved through the duplex coatings. The aim of the present study is to overview the research advances on processes of duplex coatings on (aluminum) alloys combined with micro plasma oxidation process and with other modern processes such as physical vapour deposition and plasma assisted chemical vapour deposition and also to evaluate the performance of micro plasma oxidation coatings in improving the load-bearing, friction and wear resistance properties of aluminum alloys in comparison with other coatings. Wherein, a more detailed presentation of the processes and their performances and disadvantages are given as well.
基金Project(51271012)supported by the National Natural Science Foundation of China
文摘Anodic films were successfully fabricated on Ti6A14V alloy by anodic oxidation method in an environmental friendly electrolyte with and without sodium hypochlorite. The anodic films were characterized by means of the scanning electron microscope （SEM） and energy dispersive spectrometer （EDS）. Results revealed that the addition of sodium hypochlorite leads to the ultrafast growth of oxide films, and results in the significant changes of morphology and thickness. The influence of sodium hypochlorite on formation and crystallization of oxide films as a function of anodizing time was discussed. Meanwhile, potentiodynamic electrochemical tests and dry sliding wear tests were performed to evaluate the corrosion resistance and tribological properties of oxide films. It was found that the oxide film fabricated with the existence of sodium hypochlorite had improved corrosion resistance and tribological properties than the one formed without sodium hypochlorite. Moreover, the effect mechanism of sodium hypochlorite on the growth rate and surface morphologies of oxide films during the anodizing process was discussed. It was found that hypochlorite ions participated in the reaction on anode which causes the rapid growth of oxide films and then affect the whole anodizing process.