The deep fissured rock mass is affected by coupled effects of initial ground stress and external dynamic disturbance.In order to study the effect of internal flaw on pre-stressed rock mechanical responses and failure ...The deep fissured rock mass is affected by coupled effects of initial ground stress and external dynamic disturbance.In order to study the effect of internal flaw on pre-stressed rock mechanical responses and failure behavior under impact loading,intact granite specimens and specimens with different flaw inclinations are tested by a modified split Hopkinson pressure bar(SHPB)and digital image correlation(DIC)method.The results show that peak strain and dynamic strength of intact specimens and specimens with different flaw angles(α)decrease with the increase of axial static pressure.The 90°flaw has weak reduction effect on peak strain,dynamic strength and combined strength,while 45°and 0°flaws have remarkable reduction effect.Specimens with 90°flaw are suffered combined shear and tensile failure under middle and low axial static pre-stresses,and suffered shear failure under high axial static pre-stresses.Specimens with 45°and 0°flaws are suffered oblique shear failure caused by pre-existing flaw under different axial static pre-stresses.Besides,based on digital image correlation method,it is found that micro-cracks before formation of macro fractures(include shear and tensile fractures)belong to tensile cracks.Tensile and shear strain localizations at pre-existing flaw tip for specimen with 45°and 0°flaws are produced much earlier than that at other positions.展开更多
The dynamic mechanical properties of rock specimens after thermal treatment in the air-filled environment(AE:i.e.,at the free surface)have been extensively investigated,yet they are rarely estimated in the quasi-vacuu...The dynamic mechanical properties of rock specimens after thermal treatment in the air-filled environment(AE:i.e.,at the free surface)have been extensively investigated,yet they are rarely estimated in the quasi-vacuum environment(VE:i.e.,far from free surface),which is of special importance in engineering practice.Several precise laboratory tests(i.e.,split Hopkinson pressure bar test)on marble samples in both AE and VE were performed to investigate physical and dynamic mechanical behaviors of marble after heat treatment(25℃ to 900℃)in AE and VE.The tests results demonstrate that related properties of marble could be divided into three different stages by corresponding critical temperatures of 300℃ and 600℃,at which heat damage factors are 0.29(0.30)and 0.88(0.92)in VE(AE),respectively.The thermal damage developes more fully in AE than in VE.The thermal environment plays an important role,especially in Stage 3.Specifically,a conspicuous difference(greater than 20%)between AE and VE occurs in corresponding dynamic strength and the anti-deformation capacities of tested marble specimen.The influence of heat damage of rock is very important and valuable in engineering practice,particularly when the temperature is very high(greater than 600℃).展开更多
The effect of moisture content upon compressive mechanical behavior of concrete under impact loading was studied. The axial rapid compressive loading tests of over 50 specimens with five different saturations were exe...The effect of moisture content upon compressive mechanical behavior of concrete under impact loading was studied. The axial rapid compressive loading tests of over 50 specimens with five different saturations were executed. The technique "split Hopkinson pressure bar"(SHPB) was used. The impact velocity was 10 m/s with corresponding strain rate of 50 s-1. The compressive behavior of materials was measured in terms of stress-strain curves, dynamic compressive strength, dynamic increase factor(DIF) and critical strain at a maximum stress. The data obtained from test indicate that both ascending and descending portions of stress-stain curves are affected by moisture content. However, the effect is noted to be more significant in ascending portion of the stress-strain curves. Dynamic compressive strength is higher at lower moisture content and weaker at higher moisture content.Furthermore, under nearly saturated condition, an increase in compressive strength can be found. The effect of moisture content on the average DIF of concrete is not significant. The critical compressive strain of concrete does not change with moisture content.展开更多
Since loading wave shapes are very important in the study of rock dynamical properties, a new procedure for obtaining a variety of wave shapes using equidiameter impact hammer of conventional SHPB device is proposed b...Since loading wave shapes are very important in the study of rock dynamical properties, a new procedure for obtaining a variety of wave shapes using equidiameter impact hammer of conventional SHPB device is proposed based on theoretical analysis. Experiment shows that different loading wave shapes can be obtained through varying the radius at impact end of hammer. Experiment results are quite consistent with the theoretical analysis.展开更多
Split Hopkinson Pressure Bar(SHPB) test was simulated to investigate the distribution of the first principal stress and damage zone of specimen subjected to dynamic compressive load. Numerical models of plate-type spe...Split Hopkinson Pressure Bar(SHPB) test was simulated to investigate the distribution of the first principal stress and damage zone of specimen subjected to dynamic compressive load. Numerical models of plate-type specimen containing cracks with inclined angles of 0°,45° and 90° were also established to investigate the crack propagation and damage evolution under dynamic loading. The results show that the simulation results are in accordance with the failure patterns of specimens in experimental test. The interactions between stress wave and crack with different inclined angles are different; damage usually appears around the crack tips firstly; and then more damage zones develop away from the foregoing damage zone after a period of energy accumulation; eventually,the damage zones run through the specimen in the direction of applied loading and split the specimen into pieces.展开更多
基金Project(2019JJ20028)supported by the Outstanding Youth Science Foundations of Hunan Province of ChinaProject(51774321)supported by the National Natural Science Foundation of ChinaProject(2018YFC0604606)supported by the State Key Research Development Program of China。
文摘The deep fissured rock mass is affected by coupled effects of initial ground stress and external dynamic disturbance.In order to study the effect of internal flaw on pre-stressed rock mechanical responses and failure behavior under impact loading,intact granite specimens and specimens with different flaw inclinations are tested by a modified split Hopkinson pressure bar(SHPB)and digital image correlation(DIC)method.The results show that peak strain and dynamic strength of intact specimens and specimens with different flaw angles(α)decrease with the increase of axial static pressure.The 90°flaw has weak reduction effect on peak strain,dynamic strength and combined strength,while 45°and 0°flaws have remarkable reduction effect.Specimens with 90°flaw are suffered combined shear and tensile failure under middle and low axial static pre-stresses,and suffered shear failure under high axial static pre-stresses.Specimens with 45°and 0°flaws are suffered oblique shear failure caused by pre-existing flaw under different axial static pre-stresses.Besides,based on digital image correlation method,it is found that micro-cracks before formation of macro fractures(include shear and tensile fractures)belong to tensile cracks.Tensile and shear strain localizations at pre-existing flaw tip for specimen with 45°and 0°flaws are produced much earlier than that at other positions.
基金Projects(51579239,42077240,51979280)supported by the National Natural Science Foundation of China。
文摘The dynamic mechanical properties of rock specimens after thermal treatment in the air-filled environment(AE:i.e.,at the free surface)have been extensively investigated,yet they are rarely estimated in the quasi-vacuum environment(VE:i.e.,far from free surface),which is of special importance in engineering practice.Several precise laboratory tests(i.e.,split Hopkinson pressure bar test)on marble samples in both AE and VE were performed to investigate physical and dynamic mechanical behaviors of marble after heat treatment(25℃ to 900℃)in AE and VE.The tests results demonstrate that related properties of marble could be divided into three different stages by corresponding critical temperatures of 300℃ and 600℃,at which heat damage factors are 0.29(0.30)and 0.88(0.92)in VE(AE),respectively.The thermal damage developes more fully in AE than in VE.The thermal environment plays an important role,especially in Stage 3.Specifically,a conspicuous difference(greater than 20%)between AE and VE occurs in corresponding dynamic strength and the anti-deformation capacities of tested marble specimen.The influence of heat damage of rock is very important and valuable in engineering practice,particularly when the temperature is very high(greater than 600℃).
基金Project(50979032)supported by the National Natural Science Foundation of China
文摘The effect of moisture content upon compressive mechanical behavior of concrete under impact loading was studied. The axial rapid compressive loading tests of over 50 specimens with five different saturations were executed. The technique "split Hopkinson pressure bar"(SHPB) was used. The impact velocity was 10 m/s with corresponding strain rate of 50 s-1. The compressive behavior of materials was measured in terms of stress-strain curves, dynamic compressive strength, dynamic increase factor(DIF) and critical strain at a maximum stress. The data obtained from test indicate that both ascending and descending portions of stress-stain curves are affected by moisture content. However, the effect is noted to be more significant in ascending portion of the stress-strain curves. Dynamic compressive strength is higher at lower moisture content and weaker at higher moisture content.Furthermore, under nearly saturated condition, an increase in compressive strength can be found. The effect of moisture content on the average DIF of concrete is not significant. The critical compressive strain of concrete does not change with moisture content.
文摘Since loading wave shapes are very important in the study of rock dynamical properties, a new procedure for obtaining a variety of wave shapes using equidiameter impact hammer of conventional SHPB device is proposed based on theoretical analysis. Experiment shows that different loading wave shapes can be obtained through varying the radius at impact end of hammer. Experiment results are quite consistent with the theoretical analysis.
基金Projects(50534030, 50674107, 50490274) supported by the National Natural Science Foundation of ChinaProject(06JJ3028) supported by the Provincial Natural Science Foundation of Hunan, China
文摘Split Hopkinson Pressure Bar(SHPB) test was simulated to investigate the distribution of the first principal stress and damage zone of specimen subjected to dynamic compressive load. Numerical models of plate-type specimen containing cracks with inclined angles of 0°,45° and 90° were also established to investigate the crack propagation and damage evolution under dynamic loading. The results show that the simulation results are in accordance with the failure patterns of specimens in experimental test. The interactions between stress wave and crack with different inclined angles are different; damage usually appears around the crack tips firstly; and then more damage zones develop away from the foregoing damage zone after a period of energy accumulation; eventually,the damage zones run through the specimen in the direction of applied loading and split the specimen into pieces.