Alumina ceramics are widely used in many fields such as cutting tools,laser shock materials,roadbed board and refractory.Herein,Al_(2)O_(3)ceramics are prepared by a low-cost pressureless sintering technology,using th...Alumina ceramics are widely used in many fields such as cutting tools,laser shock materials,roadbed board and refractory.Herein,Al_(2)O_(3)ceramics are prepared by a low-cost pressureless sintering technology,using the binary sintering aids of MgO and SiO_(2).The effects of sintering temperature and the ratio of binary sintering aids on the mechanical properties and microstructure of Al_(2)O_(3)ceramics are investigated.A spinel second phase(MgAl_(2)O_(4))is found out by the analysis of the results of XRD and EDS when MgO and SiO_(2)are introduced in the samples.The optimum properties are found when MgO content is 20 wt.%based on the total sintering aids and the sintering temperature is 1550℃.The bending strength and the bulk density reach a maximum value of 314 MPa and 3.73 g/cm^(3),respectively.The addition of appropriate amount of SiO_(2)makes the formation of liquid phase sintering and the removal of large pores.Meanwhile,a small amount of magnesium oxide doping has an effect on the grain refinement from the microstructure of the sample.Therefore,it is believed that MgO and SiO_(2)are the ideal sintering aids for promoting the densification and property of alumina ceramics.展开更多
基金Projects(11772207,U2130128)supported by the National Natural Science Foundation of ChinaProjects(E2019210042,E2017210065)supported by the Natural Science Foundation of Hebei Province,China+3 种基金Project(QN2019137)supported by the Natural Science Foundation of the Hebei Education Department,ChinaProject(A2019210204)supported by the Natural Science Foundation of Hebei Province for Distinguished Young Scholars,ChinaProject(216Z4302G)supported by Central Government Guiding Local Science and Technology Development,ChinaProject supported by Youth Top-notch Talents Supporting Plan of Hebei Province,China。
文摘Alumina ceramics are widely used in many fields such as cutting tools,laser shock materials,roadbed board and refractory.Herein,Al_(2)O_(3)ceramics are prepared by a low-cost pressureless sintering technology,using the binary sintering aids of MgO and SiO_(2).The effects of sintering temperature and the ratio of binary sintering aids on the mechanical properties and microstructure of Al_(2)O_(3)ceramics are investigated.A spinel second phase(MgAl_(2)O_(4))is found out by the analysis of the results of XRD and EDS when MgO and SiO_(2)are introduced in the samples.The optimum properties are found when MgO content is 20 wt.%based on the total sintering aids and the sintering temperature is 1550℃.The bending strength and the bulk density reach a maximum value of 314 MPa and 3.73 g/cm^(3),respectively.The addition of appropriate amount of SiO_(2)makes the formation of liquid phase sintering and the removal of large pores.Meanwhile,a small amount of magnesium oxide doping has an effect on the grain refinement from the microstructure of the sample.Therefore,it is believed that MgO and SiO_(2)are the ideal sintering aids for promoting the densification and property of alumina ceramics.