In order to analyze the influences of storage aging on the safety of typical elemental explosives,the aged cyclotrimethylene trinitramine(RDX)and cyclotetramethylene tetranitramine(HMX)were prepared by isothermal agin...In order to analyze the influences of storage aging on the safety of typical elemental explosives,the aged cyclotrimethylene trinitramine(RDX)and cyclotetramethylene tetranitramine(HMX)were prepared by isothermal aging tests.The reaction thresholds of aged RDX and HMX under any ignition probability were studied by Langlie-Optimal D method.The thermal decomposition characteristics of RDX and HMX after aging were analyzed by DSC and ARC.Experimental results showed that compared with unaged RDX and HMX,on the one hand,the critical impact energy and critical friction of RDX and HMX aged for 14,28,and 56 days are significantly reduced at an explosion probability of 50%,0.01%,and 0.0001%,respectively.With the increase of aging time,the mechanical sensitivity of RDX and HMX increases obviously.On the other hand,the initial decomposition temperature of RDX and HMX after 56 days of aging decreases,the decomposition heat decreases,the activation energy increases,and the reaction difficulty increases.展开更多
For Gu-Ag alloy, an important parameter called workability in the forming process of materials can be evaluated by processing maps yielded from the stress-strain data generated by hot compression tests at temperatures...For Gu-Ag alloy, an important parameter called workability in the forming process of materials can be evaluated by processing maps yielded from the stress-strain data generated by hot compression tests at temperatures of 700-850 °C and strain rates of 0.01-10 s-1. And at the true strain of 0.15, 0.35 and 0.55, respectively, the responses of strain-rate sensitivity, power dissipation efficiency and instability parameter to temperature and strain rate were studied. Instability maps and power dissipation maps were superimposed to form processing maps, which reveal the determinate regions where individual metallurgical processes occur and the limiting conditions of flow instability regions. Furthermore, the optimal processing parameters for bulk metal working are identified clearly by the processing maps.展开更多
Hexagonal boron nitride nanosheets(HBNNSs)have huge potential in the field of coating materials owing to their remarkable chemical stability,mechanical strength and thermal conductivity.Thin-layer hBNNSs were obtained...Hexagonal boron nitride nanosheets(HBNNSs)have huge potential in the field of coating materials owing to their remarkable chemical stability,mechanical strength and thermal conductivity.Thin-layer hBNNSs were obtained by a liquid-phase exfoliation of h-BN powders and incorporated into EVA coatings for improving the safety performance of 1,3,5,7-tetranitro-1,3,5,7-tetrazocane(HMX).HBNNSs and ethylene-vinyl acetate copolymer(EVA)were introduced to HMX by a solvent-slurry process.For comparison,the HMX/EVA and HMX/EVA/graphene(HMX/EVA/G)composites were also prepared by a similar process.The morphology,crystal form,surface element distribution,thermal decomposition property and impact sensitivity of HMX/EVA/hBNNSs composites were contrastively investigated.Results showed that as prepared HMX/EVA/hBNNSs composites were well coated with hBNNSs and EVA,and exhibited better thermal stability and lower impact sensitivity than that of HMX/EVA and HMX/EVA/G composites,suggesting superior performance of desensitization of hBNNSs in explosives.展开更多
基金supported by the National Key Laboratory of Energetic Materials, China (Grant No. 2023-LB-036-09).
文摘In order to analyze the influences of storage aging on the safety of typical elemental explosives,the aged cyclotrimethylene trinitramine(RDX)and cyclotetramethylene tetranitramine(HMX)were prepared by isothermal aging tests.The reaction thresholds of aged RDX and HMX under any ignition probability were studied by Langlie-Optimal D method.The thermal decomposition characteristics of RDX and HMX after aging were analyzed by DSC and ARC.Experimental results showed that compared with unaged RDX and HMX,on the one hand,the critical impact energy and critical friction of RDX and HMX aged for 14,28,and 56 days are significantly reduced at an explosion probability of 50%,0.01%,and 0.0001%,respectively.With the increase of aging time,the mechanical sensitivity of RDX and HMX increases obviously.On the other hand,the initial decomposition temperature of RDX and HMX after 56 days of aging decreases,the decomposition heat decreases,the activation energy increases,and the reaction difficulty increases.
基金Project(CSTC2009BA4065) supported by the Chongqing Natural Science Foundation,China
文摘For Gu-Ag alloy, an important parameter called workability in the forming process of materials can be evaluated by processing maps yielded from the stress-strain data generated by hot compression tests at temperatures of 700-850 °C and strain rates of 0.01-10 s-1. And at the true strain of 0.15, 0.35 and 0.55, respectively, the responses of strain-rate sensitivity, power dissipation efficiency and instability parameter to temperature and strain rate were studied. Instability maps and power dissipation maps were superimposed to form processing maps, which reveal the determinate regions where individual metallurgical processes occur and the limiting conditions of flow instability regions. Furthermore, the optimal processing parameters for bulk metal working are identified clearly by the processing maps.
基金The project was supported by Equipment Pre-research Key Laboratory Fund(No.6142020305)The authors would like to thank Shiyanjia Lab(www.shiyanjia.com)for the support of XPS test.
文摘Hexagonal boron nitride nanosheets(HBNNSs)have huge potential in the field of coating materials owing to their remarkable chemical stability,mechanical strength and thermal conductivity.Thin-layer hBNNSs were obtained by a liquid-phase exfoliation of h-BN powders and incorporated into EVA coatings for improving the safety performance of 1,3,5,7-tetranitro-1,3,5,7-tetrazocane(HMX).HBNNSs and ethylene-vinyl acetate copolymer(EVA)were introduced to HMX by a solvent-slurry process.For comparison,the HMX/EVA and HMX/EVA/graphene(HMX/EVA/G)composites were also prepared by a similar process.The morphology,crystal form,surface element distribution,thermal decomposition property and impact sensitivity of HMX/EVA/hBNNSs composites were contrastively investigated.Results showed that as prepared HMX/EVA/hBNNSs composites were well coated with hBNNSs and EVA,and exhibited better thermal stability and lower impact sensitivity than that of HMX/EVA and HMX/EVA/G composites,suggesting superior performance of desensitization of hBNNSs in explosives.