An investigation on damage location due to the corrosion in reinforced concrete structures is conducted. The frequency change square ratio is used as a parameter for the damage. It is theoretically verified that the p...An investigation on damage location due to the corrosion in reinforced concrete structures is conducted. The frequency change square ratio is used as a parameter for the damage. It is theoretically verified that the parameter is a function of the damage location. Experimental results of the corrosion in reinforced concrete structures show that the predicted damage location is in agreement with the real damage location. The modal parameters are used to detect the damages in structural concrete elements, and so they are useful for structural appraisal.展开更多
The steel corrosion in concrete is widely reported over the last two to three decades. Much effort has been devoted to researching the causes and mechanisms of reinforcement corrosion and to the questions of durabilit...The steel corrosion in concrete is widely reported over the last two to three decades. Much effort has been devoted to researching the causes and mechanisms of reinforcement corrosion and to the questions of durability for concrete structures, but relatively little attention has been devoted to the problem of assessing the effect of bond loss due to corrosion on the structural behavior of corroded elements. From the test results on corroded specimens, the mechanism of degradation in bond behavior between corroded bars and concrete, and the effects of bond loss on structural performances are summarized. Results show that corrosion level, cover depth-W-bar diameter ratio, surface condition of re/nforcement, stirrups, etc. can influence the bond behavior of corroded bars. In addition, the deterioration in bond due to corrosion may induce reduction in bearing capacity, degradation of serviceability, and the loss in ductility for steel-corroded concrete members.展开更多
文摘An investigation on damage location due to the corrosion in reinforced concrete structures is conducted. The frequency change square ratio is used as a parameter for the damage. It is theoretically verified that the parameter is a function of the damage location. Experimental results of the corrosion in reinforced concrete structures show that the predicted damage location is in agreement with the real damage location. The modal parameters are used to detect the damages in structural concrete elements, and so they are useful for structural appraisal.
基金The Liaoning Province CommunicationDepartment Key Science Foundation (No.0101)
文摘The steel corrosion in concrete is widely reported over the last two to three decades. Much effort has been devoted to researching the causes and mechanisms of reinforcement corrosion and to the questions of durability for concrete structures, but relatively little attention has been devoted to the problem of assessing the effect of bond loss due to corrosion on the structural behavior of corroded elements. From the test results on corroded specimens, the mechanism of degradation in bond behavior between corroded bars and concrete, and the effects of bond loss on structural performances are summarized. Results show that corrosion level, cover depth-W-bar diameter ratio, surface condition of re/nforcement, stirrups, etc. can influence the bond behavior of corroded bars. In addition, the deterioration in bond due to corrosion may induce reduction in bearing capacity, degradation of serviceability, and the loss in ductility for steel-corroded concrete members.