Surface tension of calcium aluminate refining slag was measured by the Slide method at 1823 K.Based on different levels of the MgO content and the mass ratio of CaO to Al_2O_3,the effects of MgO content and the mass r...Surface tension of calcium aluminate refining slag was measured by the Slide method at 1823 K.Based on different levels of the MgO content and the mass ratio of CaO to Al_2O_3,the effects of MgO content and the mass ratio of CaO to Al_2O_3 on surface tension were investigated.The results indicate that surface tension decreased with increasing MgO content(from 0 to 4.86%),followed by an increase with further increasing MgO content up to 11.33%.The trend that surface tension changed with the mass ratio of CaO to Al_2O_3 was the same as the trend that surface tension changed with the MgO content.The surface tension was varied from 0.617 N/m to 0.710 N/m,for the mass ratio of CaO to Al_2O_3 varying between 0.60 and 1.28.An attempt was made to estimate surface tension of CaO-Al_2O_3-MgO slag and its sub-system,and the application showed that the model worked well.展开更多
基金Project(51204115)supported by the National Natural Science Foundation of ChinaProject(BK20130308)supported by the Basic Research Program of Jiangsu Province,ChinaProject(2014M561710)supported by China Postdoctoral Science Foundation
文摘Surface tension of calcium aluminate refining slag was measured by the Slide method at 1823 K.Based on different levels of the MgO content and the mass ratio of CaO to Al_2O_3,the effects of MgO content and the mass ratio of CaO to Al_2O_3 on surface tension were investigated.The results indicate that surface tension decreased with increasing MgO content(from 0 to 4.86%),followed by an increase with further increasing MgO content up to 11.33%.The trend that surface tension changed with the mass ratio of CaO to Al_2O_3 was the same as the trend that surface tension changed with the MgO content.The surface tension was varied from 0.617 N/m to 0.710 N/m,for the mass ratio of CaO to Al_2O_3 varying between 0.60 and 1.28.An attempt was made to estimate surface tension of CaO-Al_2O_3-MgO slag and its sub-system,and the application showed that the model worked well.