A high-performance porous carbon material for supercapacitor electrodes was prepared by using a polymer blend method. Phenol-formaldehyde resin and gelatin were used as carbon precursor polymer and pore former polymer...A high-performance porous carbon material for supercapacitor electrodes was prepared by using a polymer blend method. Phenol-formaldehyde resin and gelatin were used as carbon precursor polymer and pore former polymer, respectively. The blends were carbonized at 800℃ in nitrogen. SEM, BET measurement and BJH method reveal that the obtained carbon possesses a mesoporous characteristic, with the average pore size between 3.0 nm and 5.0 nm. The electrochemical properties of supercapacitor using these carbons as electrode material were investigated by cyclic voltammetry and constant current charge-discharge. The results indicate that the composition of blended polymers has a strong effect on the specific capacitance. When the mass ratio of PF to gelatin is kept at 1：1, the largest surface area of 222 m2/g is obtained, and the specific capacitance reaches 161 F/g.展开更多
基金Projects(50772033,50972043) supported by the National Natural Science Foundation of ChinaProject(09JJ3095) supported by the Natural Science Foundation of Hunan Province,China+2 种基金Project(09A001) supported by the Scientific Research Fund of Hunan Provincial Education Department,ChinaProject(2010FJ3151) supported by the Science and Research Plan of Hunan Province,ChinaProject supported by the Science and Technology Innovative Research Team in Higher Education Institution of Hunan Province,China
文摘A high-performance porous carbon material for supercapacitor electrodes was prepared by using a polymer blend method. Phenol-formaldehyde resin and gelatin were used as carbon precursor polymer and pore former polymer, respectively. The blends were carbonized at 800℃ in nitrogen. SEM, BET measurement and BJH method reveal that the obtained carbon possesses a mesoporous characteristic, with the average pore size between 3.0 nm and 5.0 nm. The electrochemical properties of supercapacitor using these carbons as electrode material were investigated by cyclic voltammetry and constant current charge-discharge. The results indicate that the composition of blended polymers has a strong effect on the specific capacitance. When the mass ratio of PF to gelatin is kept at 1：1, the largest surface area of 222 m2/g is obtained, and the specific capacitance reaches 161 F/g.