In order to improve the scheelite flotation with sodium oleate(NaOL),the effect of a non-ionic polyoxyethylene ether(JFC-5)on the floatability of scheelite was investigated through flotation experiments at10°C,co...In order to improve the scheelite flotation with sodium oleate(NaOL),the effect of a non-ionic polyoxyethylene ether(JFC-5)on the floatability of scheelite was investigated through flotation experiments at10°C,compared with60mg/L NaOL alone,the recovery of scheelite is improved from22%to85%in the presence of JFC-5with a mass ratio of20%at pH10.Moreover,the resistance to Ca2+of NaOL is increased.The adsorption mechanism was analyzed by zeta potential measurement,contact angle measurement and X-ray photoelectron spectroscopy(XPS)analysis.The results show that the adsorption of NaOL on scheelite surface is enhanced after adding JFC-5due to the more negative zeta potentials and larger contact angles of scheelite.And the co-adsorption of NaOL and JFC-5is confirmed by XPS analysis,so it is indicated that the adsorption of JFC-5decreases the electrostatic repulsion between the oleate ions,resulting in the stronger adsorption of NaOL on scheelite surface.In short,the mixed NaOL/JFC-5collector can effectively improve scheelite flotation.展开更多
The wettability,surfactivity and the correlation between wettability and surfactivity of sodium diethylhexylphosphate,sodium diethylhexyl polyoxyethylene phosphate and their complex in NaOH solutions were studied.A co...The wettability,surfactivity and the correlation between wettability and surfactivity of sodium diethylhexylphosphate,sodium diethylhexyl polyoxyethylene phosphate and their complex in NaOH solutions were studied.A complex alkali resistant phosphate surfactant with good permeability was prepared.The wettability of surfactants was investigated by measuring the immersion time,sinking time and capillary effects of nature cotton grey fabric in NaOH solutions.The surfactivity of the surfactants was characterized by measuring the surface tension.The effect of the complex on the surface appearance of cotton grey fabric was also investigated with a scanning electron microscope(SEM) .The results show that all the surfactants exhibit good wettability for cotton grey fabric in 0.5-5.0 mol/L of NaOH solutions,the complex system exhibits better wettability in 5.0-7.0 mol/L of NaOH solutions,in comparison with either corresponding single surfactant component employed,and wettability is well correlative with the surfactivities of the surfactant.SEM images indicate that the cotton grey fabric is well wetted by the alkaline surfactant solution and the quality of fabric is improved.展开更多
基金Project(2016RS2016)supported by Hunan Provincial Science and Technology Leader(Innovation Team of Interface Chemistry of Efficient and Clean Utilization of Complex Mineral Resources)China
文摘In order to improve the scheelite flotation with sodium oleate(NaOL),the effect of a non-ionic polyoxyethylene ether(JFC-5)on the floatability of scheelite was investigated through flotation experiments at10°C,compared with60mg/L NaOL alone,the recovery of scheelite is improved from22%to85%in the presence of JFC-5with a mass ratio of20%at pH10.Moreover,the resistance to Ca2+of NaOL is increased.The adsorption mechanism was analyzed by zeta potential measurement,contact angle measurement and X-ray photoelectron spectroscopy(XPS)analysis.The results show that the adsorption of NaOL on scheelite surface is enhanced after adding JFC-5due to the more negative zeta potentials and larger contact angles of scheelite.And the co-adsorption of NaOL and JFC-5is confirmed by XPS analysis,so it is indicated that the adsorption of JFC-5decreases the electrostatic repulsion between the oleate ions,resulting in the stronger adsorption of NaOL on scheelite surface.In short,the mixed NaOL/JFC-5collector can effectively improve scheelite flotation.
基金Project(20573079) supported by the National Natural Science Foundation of China
文摘The wettability,surfactivity and the correlation between wettability and surfactivity of sodium diethylhexylphosphate,sodium diethylhexyl polyoxyethylene phosphate and their complex in NaOH solutions were studied.A complex alkali resistant phosphate surfactant with good permeability was prepared.The wettability of surfactants was investigated by measuring the immersion time,sinking time and capillary effects of nature cotton grey fabric in NaOH solutions.The surfactivity of the surfactants was characterized by measuring the surface tension.The effect of the complex on the surface appearance of cotton grey fabric was also investigated with a scanning electron microscope(SEM) .The results show that all the surfactants exhibit good wettability for cotton grey fabric in 0.5-5.0 mol/L of NaOH solutions,the complex system exhibits better wettability in 5.0-7.0 mol/L of NaOH solutions,in comparison with either corresponding single surfactant component employed,and wettability is well correlative with the surfactivities of the surfactant.SEM images indicate that the cotton grey fabric is well wetted by the alkaline surfactant solution and the quality of fabric is improved.